按天然白云石(≤0.1 mm)与工业氧化铝粉(≤0.088 mm)的质量比为45∶55配料,经混合、成型和烘干后,于1 600℃3 h煅烧,细磨烧结体得到含镁铝尖晶石的新型铝酸盐水泥.测量了新型铝酸盐水泥的凝结时间、耐火度以及用其所结合高铝矾土制成的耐火浇注料的早期强度;利用XRD、SEM和EDS分析了新型铝酸盐水泥的物相组成及其形貌和分布,同时采用静态坩埚法对比了新型铝酸盐水泥和纯铝酸钙水泥结合刚玉浇注料的抗渣性差异.结果表明:新型水泥的物相组成为镁铝尖晶石(MA)、一铝酸钙(CA)和二铝酸钙(CA2),且这3个物相的分布较为均匀;新型水泥的凝结时间正常,耐火度高于纯铝酸钙水泥;用新型水泥制得的刚玉浇注料抗渣性好;其原因是新型水泥组成中引入了镁铝尖晶石相,而镁铝尖晶石具有较高的熔点和抗熔渣侵蚀能力.
参考文献
| [1] | Ghosh A;Sarkar Ritwik;Mukherjee B et al.Effect of spinel content on the properties of magnesia-spinel composite refractory[J].Journal of the European Ceramic Society,2004,24(12):2079-2085. |
| [2] | Mukhopadhyay S;Dss Poddar P K .Effect of preformed and in situ spinels on microstructure and properties of a low cement refractory csstable[J].Ceramics International,2004,30(04):369-380. |
| [3] | Sarpoolaky H;Zhang S;Lee W L .Corrosion of high alumina and near stoichiometric spinels in iron-containing silicate slags[J].Journal of the European Ceramic Society,2003,23(03):293-300. |
| [4] | Cho M K;Hong G G;Lee S K .Corrosion of spinel clinker by CaOAl2O3 -SiO2 ladle slag[J].Journal of the European Ceramic Society,2002,22(10):1983-1990. |
| [5] | Lee W E;Moore R E .Evolution of in situ refractories in the 20th century[J].Journal of The American Chemical Society,1998,81(06):1385-1410. |
| [6] | Korgul P;Wilson D R;Lee W E .Microstructural analysis of corroded alumina-spinel castable refractories[J].Journal of the European Ceramic Society,1997,17(01):77-84. |
| [7] | Studart A R;Ortega F;Innocentini M D M .Gel casting high alumina refractory castable[J].Journal of The American Chemical Society,2002,81(01):42-46. |
| [8] | 关振铎;张中太;焦金生.无机材料物理性能[M].北京:清华大学出版社,1998:126-127. |
| [9] | 李晓明;吴清顺;蔡飞虎.特种不定形耐火材料及不烧耐火砖[M].北京:冶金工业出版社,1992:18-19. |
| [10] | Nagy M A;El-Hemaly S A S;Lamey G G .Aluminous cements containing magnesium aluminate spinel from Egyptian dolomite[J].Ceramics International,2001,27(08):865-873. |
| [11] | A.H. De Aza;P. Pena;M.A. Rodriguez .New spinel-containing refractory cements[J].Journal of the European Ceramic Society,2003(5):737-744. |
| [12] | 金格瑞 W D;清华大学无机非金属材料教研组.陶瓷导论[M].北京:中国建筑工业出版社,1988:416-426. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%