借助扫描电镜和能谱仪研究了一种Al2O3-ZrO2-C系滑板的侵蚀作用.结果呈现出两种形式:1)形成不含FeO的反应带和较厚的脱炭层;2)形成含FeO的反应带和较薄的脱炭层.两种类型的侵蚀行为导致显微结构演变之差异,由各种生成相的3D形貌得以充分地展示.MgO-CaO-Al2O3-SiO2系熔渣与滑板相互反应的主要生成相为MA和黄长石类硅酸盐;而有FeO参与反应者,生成组成广泛的FA系尖晶石固溶体、RO固溶体和黄长石类硅酸盐.
参考文献
| [1] | 王天仇.滑板的研制与发展简述[C].2004年全国耐火材料综合学术年会论文集,2004:200-205. |
| [2] | К В Cимонов.Иэносмагнеэиалъныхплитпри 6есстопорнойраэливкестали[J].Огнеупоры,1975(08):31-37. |
| [3] | Deilmann W;Grabner B;Krause O.über den Verschleiss vanSchieberverschlüssen[J].Radex-Rundschau,1977(01):3-14. |
| [4] | Deilmann W;Grabner B.Weiterentwicklung van basischen Keramikteilen für Schieberverschlüsse[J].Radex-Rundschau,1979(04):1156-1168. |
| [5] | Furumi K;Semba K;Shikanо H.Wear pattern of plate brick in sliding gate nozzle process[J].Interceram,1980(01):49-52. |
| [6] | Itoh K;Fushimi T.Reaction between slide gate plate and boron contained steel[J].耐水物,1998(12):644-650. |
| [7] | Uchida S;Lin W.Microstructure of spinel SEN used for casting highoxygen,calcium-streated,free-cutting and high-manganese steels[J].Shinagawa Tech Report,2001(44):47-56. |
| [8] | 高振昕;平增福;张战营.耐火材料显微结构[M].北京:冶金工业出版社,2002:250-251. |
| [9] | 高振昕,周宁生,王天仇,梁兰芳.TiO2在Al2O3-ZrO2电熔料共晶体中的固溶行为[J].硅酸盐学报,2005(09):1145-1148. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%