设计不同的水泥熟料物相组成,以石灰石、重烧氧化镁和铝矾土熟料为原料,于1400℃3 h处理后制备了含不同量镁铝尖晶石相的铝酸盐水泥.利用XRD和SEM对不同配比的合成产物的物相及形貌特征进行了分析,并对这种新型铝酸盐水泥浇注料进行了抗压强度的测试.结果表明:含镁铝尖晶石的铝酸盐水泥的主要物相为一铝酸钙(CA)、镁铝尖晶石(MA)和二铝酸钙(CA2),还有少量的硅铝酸二钙(C2AS)和残余刚玉(α-Al2O3);浇注料的强度随MA含量的减小而增大,且随水化时间延长,其强度增进稳定.
参考文献
| [1] | Ghosh A;Sarkar Ritwik;Mukherjee B et al.Effect of spinel content on the properties of magnesia-spinel composite refractory[J].Journal of the European Ceramic Society,2004,24(12):2079-2085. |
| [2] | Mukhopedhyay S;Das Poddar P K .Effect of preformed and in situ spinels on microstructure and propertiea of a low cement refractory castable[J].Ceramics International,2004,30(04):369-380. |
| [3] | Sarpeolaky H;Zhang S;Lee W E .Corrosion of high alumina and near stoichiometric spinels in iron-containing silicate slags[J].Journal of the European Ceramic Society,2003,23(03):293-300. |
| [4] | 肖国庆,高云琴,段锋.含镁铝尖晶石的铝酸盐水泥的制备及其抗侵蚀性[J].硅酸盐学报,2008(08):1172-1177. |
| [5] | Nagy M A;El-Hemaly S A S;Lamey G G .Aluminous cements containing magnegium aluminate spinel from Egyptian dolomite[J].Ceramics International,2001,27(08):865-873. |
| [6] | A.H. De Aza;P. Pena;M.A. Rodriguez .New spinel-containing refractory cements[J].Journal of the European Ceramic Society,2003(5):737-744. |
| [7] | 肖国庆,高志鹏,荆桂花,庞锐.新型含镁铝尖晶石的铝酸盐水泥的研究[J].西安建筑科技大学学报（自然科学版）,2005(03):411-415. |
| [8] | 李建平,谢玉玲.镁铝尖晶石的合成及其工业应用[J].非金属矿,1996(04):24-27. |
| [9] | 段锋,肖国庆,荆桂花,张君博,高云琴.含镁铝尖晶石的铝酸盐水泥的制备与应用[J].耐火材料,2007(01):41-44,53. |
| [10] | 刘光华,张进生.高铝水泥与硅酸盐水泥混合物的耐久性[C].第二届中国国际建筑干混砂浆生产应用技术研讨会论文集,2006:83-88. |
| [11] | Cox J D;Sharp J H.The use of admixtures with calcium aluminate cements[A].Karlsruhe,Germany,1994:381-385. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%