以工业硅溶胶为原料,通过凝胶过程与干燥条件的控制,采用常压干燥法制备了SiO2 气凝胶粉体,并考察了老化液中正硅酸乙脂(TEOS)含量和干燥控制化学添加荆甲酰胺的添加对气凝胶粉体堆积密度、比表面积和孔径分布的影响.结果表明:所得气凝胶粉体具有纳米多孔结构,组成气凝胶结构的基本粒子呈圆球形,粒径为10～25 nm,由基本粒子连接而成的网络结构具有5～50 nm的孔径分布;随着热处理温度从常温升至1 100℃,SiO2气凝胶从最初的无定形态转化为方石英;在,TEOS的醇溶液中老化,有利于增强凝胶骨架的强度;添加甲酰胺可以改善气凝胶粉体的孔径分布,提高其比表面积.
参考文献
| [1] | A. Soleimani Dorcheh;M. H. Abbasi .Silica aerogel; synthesis, properties and characterization[J].Journal of Materials Processing Technology,2008(1-3):10-26. |
| [2] | Bhagat SD;Hirashima H;Rao AV .Low density TEOS based silica aerogels using methanol solvent[J].Journal of Materials Science,2007(9):3207-3214. |
| [3] | Lu X;Arduini-Schuster M C;Kuhn J et al.Thermal conductivity of monolithic organic aerogels[J].Science,1992,225(5047):971-972. |
| [4] | Sung-Woo Hwang;Hae-Hyun Jung;Sang-Hoon Hyun .Effective preparation of crack-free silica aerogels via ambient drying[J].Journal of Sol-Gel Science and Technology,2007(2):139-146. |
| [5] | 陈龙武;甘礼华.气凝胶[J].化学通报(印刷版),1997(08):21-27. |
| [6] | Fei Shi;Lijiu Wang;Jingxiao Liu .Synthesis and characterization of silica aerogels by a novel fast ambient pressure drying process[J].Materials Letters,2006(29/30):3718-3722. |
| [7] | Bhagat, SD;Kim, YH;Ahn, YS;Yeo, JG .Textural properties of ambient pressure dried water-glass based silica aerogel beads: One day synthesis[J].Microporous and Mesoporous Materials,2006(1/3):237-244. |
| [8] | 甘礼华,张宇星,陈龙武,葛奇.干燥控制化学添加剂在制备硅气凝胶中的应用[J].同济大学学报(自然科学版),2003(09):1131-1134. |
| [9] | Parashar V K;Raman V;Bahl O P et al.Dimethylformamide and glycol in the preparation and properties of sol-gel derived silica[J].Journal of Materials Science,1996,15(16):1403-1407. |