以电熔白刚玉、电熔莫来石、氧化铝微粉、二氧化硅微粉和硅溶胶为主要原料,制备了硅溶胶、二氧化硅微粉结合刚玉浇注料以及硅溶胶结合刚玉-莫来石浇注料,研究了不同温度处理后浇注料的常温性能、冷态和热态抗折强度以及弹性模量等性能,并进行了差热、X射线衍射和显微结构分析.研究结果表明:1)与二氧化硅微粉相比,硅溶胶能够显著提高浇注料800℃以下的抗折强度；硅溶胶结合和二氧化硅微粉结合的机制以及随温度变化的规律基本一致.2)高温下刚玉骨料中β-Al2O3分解产生的Na2O大部分进入液相,使液相中Na2O含量增加,不利于浇注料中原位生成莫来石,并降低材料的高温强度.3)莫来石加入到硅溶胶结合刚玉浇注料中,能显著降低浇注料的弹性模量,借助于高温下液相的传质作用,莫来石彼此连接形成网络,从而增加了浇注料的强度.
参考文献
| [1] | A.R.Studart W.Zhong and V.C.Pan .Rheological design of zero-cement self-flow castables[J].American Ceramic Society bulletin,1999(785):65-72. |
| [2] | Gerotto M.V.;Studart A.R. .Zero-Cement, High-Alumina Castables[J].American Ceramic Society bulletin,2000(9):75-84. |
| [3] | L. Mandecka-Kamien;K. Makuch .Active Aluminas for the Production of Zero-cement Refractory Castables[J].Interceram: International Journal for Bricks, Structural Clay Products, Refractories, Pottery, Fine Ceramics, Abrasives and Special Ceramics,2005(3):178-181. |
| [4] | Khalil N M .Heat resistance and thermomechanical behaviour of ultralow and zero cement castables[J].British Ceramic Transactions,2004,103(01):37-41. |
| [5] | Studart A R;Pandolfelli V C .Thermomechanical behavior of zerocement,high-alumina castables[J].American Ceramic Society Bulletin,2000,79(10):53-60. |
| [6] | Zawrah M F;Khalil N M .Effect of mullite formation on proerties of refractory castables[J].Ceramics International,2001,27(06):689-694. |
| [7] | 田华,陈连喜,刘全文.硅溶胶的性质、制备和应用[J].国外建材科技,2007(02):8-11,17. |
| [8] | Zhu X;Jiang D;Tan S et al.Dispersion properties of alumina powders in silica sol[J].Journal of the European Ceramic Society,2001,21(16):2879-2885. |
| [9] | 卫晓辉,孙加林,孙庚辰.莫来石的低温合成[J].耐火材料,2008(03):229-231,233. |
| [10] | 熊继全,代洁,彭云涛,方昌荣,任强,程鹏.硅溶胶结合刚玉-莫来石浇注料的研制及应用[J].耐火材料,2011(02):110-111,114. |
| [11] | 曾伟,王玺堂,张保国.添加剂对硅溶胶结合刚玉浇注料流动性和常温物理性能的影响[J].武汉科技大学学报（自然科学版）,2008(06):570-573. |
| [12] | R.D. dos Anjos;M.R. Ismael;I.R. de Oliveira .Workability and setting parameters evaluation of colloidal silica bonded refractory suspensions[J].CERAMICS INTERNATIONAL,2008(1):165-171. |
| [13] | Risbud S H;Pask J A .SiO2-Al2O3 metastable phase equilibrium diagram without mullite[J].Journal of Materials Science,1978,13(11):2449-2454. |
| [14] | 陈桂华,杨辉,王家邦,孔德玉.莫来石结合莫来石-刚玉质高温推板的研制[J].硅酸盐学报,2002(z1):105-108. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%