以AIN-Y2O3-La2O3为烧结助剂,在5.5 GPa,1 550℃下对c-BN-β-Si3N4复合材料进行了超高压烧结.借助X射线及扫描电镜对烧结样品进行了分析和观察,探讨了保温时间对产物的组成、形貌及力学性能的影响.结果表明:1)超高压条件下c-BN保持了原有的结构及形貌,发育良好的棒状β-Si3N4晶体均匀分布于烧结体中;α-Si3N4完全转变成β-Si3N4的时间随c-BN含量的增加而延长;烧结体相对密度和弯曲强度均随c-BN含量的增加而降低,硬度则随着c-BN含量的增加而增加,而相对密度的降低在一定程度上抵消了c-BN对硬度提高的贡献.2)c-BN质量分数为50%的复合材料同时具备较高的弯曲强度及硬度,其值分别为830 MPa与29.3 GPa.

参考文献

[1] Yucheng Zhao;Mingzhi Wang .Effect of sintering temperature on the structure and properties of polycrystalline cubic boron nitride prepared by SPS[J].Journal of Materials Processing Technology,2009(1):355-359.
[2] Ye, F.;Hou, Z.;Zhang, H.;Liu, L.;Zhou, Y. .Spark plasma sintering of cBN/β-SiAlON composites[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2010(18/19):4723-4726.
[3] Mikinori Hotta;Takashi Goto .Densification and Phase Transformation of β-SiAlON-Cubic Boron Nitride Composites Prepared by Spark Plasma Sintering[J].Journal of the American Ceramic Society,2009(8):1684-1690.
[4] Hotta M;Goto T .Effect of time on microstructure and hardness of β-SiAlON-cubic boron nitride composites during spark plasma sintering[J].Ceramics International,2011,37(02):521-524.
[5] Hotta M;Goto T .Densification,phase transformation and hardness of mullite-cubic BN composites prepared by spark plasma sintering[J].Journal of the Ceramic Society of Japan,2010,118(02):157-160.
[6] Hotta M;Goto T.Spark plasma sintering of β-SiAlON-c-BN composite[J].Materials Science Forum,2011(561-565):1453-1457.
[7] Endo T;Fukunga O;Iwata M .The synthesis of c-BN using Ca3B2N4[J].Journal of Materials Science,1981,16(08):2227-2232.
[8] 沈中毅;孙继荣;刘世超 等.A study on sintering behavior of silicon nitride Si3N4 micro-powder under high pressure[J].Chinese Journal of High Pressure Physics,1991,5(04):267-273.
[9] 唐翠霞,唐敬友,姚怀,寇自力,刘雨生,贺红亮,杨世源.添加Y2O3-Al2O3烧结助剂的氮化硅陶瓷的超高压烧结[J].硅酸盐学报,2007(07):828-831.
[10] 祖义忠,唐敬友,唐翠霞.高温高压下α-Si3N4的相变[J].北京科技大学学报,2009(02):215-219.