通过观察损毁样品的侵蚀和渗透情况,研究浇铸TRIP钢时保护渣对ZrO2-C渣线材料的侵蚀机制.ZrO2及其稳定剂CaO的侵蚀溶解是渣线材料侵蚀的决定因素.氧化是石墨损毁的主要方式,石墨在钢水里的溶解对其损毁不起重要作用.ZrO2溶解量和石墨氧化量的比值随着热面到钢水垂直距离的减少而减少.然而,与其他炼钢用碳结合耐火材料不同,在本研究的特殊情况下,石墨被保护渣浸润,它仍然充当耐火成分,但仅部分作为抗渣渗透剂.渣渗透后,ZrO2开始被侵蚀,降低了抗渣侵蚀性,然而渣中成分的气相传输可能导致CaO在未渗透区域脱溶.
参考文献
| [1] | Hauck F;P(o)tschke J .Der Verschleiβ von Tauchausgüssen beim Stranggieβen von Stahl[J].Arch Eisenhüttenwes,1982,53:133-138. |
| [2] | Mukai K;Toguri J M;Stubina N M et al.A mechanism for the local corrosion of immersion nozzles[J].ISIJ International,1989,29(06):469-476. |
| [3] | Heikkinen E P;Mattila R A;Kokkonen T M T et al.The chemical wear of the SEN-slagline in the continuous casting of stainless steels[J].Steelmaking Conf,2002,85:419-428. |
| [4] | Brandaleze E;Gorosurreta C.SEN wear mechanism associated to Marangoni effect during continuous casting[A].Buenos Aires,Argentina,2003:629-638. |
| [5] | Aiba Y;Oki K;Sugie M et al.Study of corrosion and penetration of zirconia refractories by molten steel and slag[J].Taikabutsu Overseas,1985,5(01):3-11. |
| [6] | Lee Y M;Yin H.Zirconia graphite wear and steel inclusions[A].Vancouver,Canada,2010:221-223. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%