为了改善氧化铝空心球的抗铝液浸润性能及强度,采用纳米硫酸钡对氧化铝空心球进行表面涂覆.以氯化钡、硫酸铵和EDTA二钠盐为原料,采用液相法在室温、pH =5.0的条件下制得纳米硫酸钡乳液,再用此乳液对氧化铝空心球进行涂覆,并分别在400、600、800、1 000℃下进行热处理.然后采用SEM观察了涤覆前后氧化铝空心球表面的显微结构特征,并进行了抗铝液浸润性及耐压强度测试.结果表明:随着热处理温度的升高,空心球表面涂层的致密度和均匀性提高,经1 000℃热处理的氧化铝空心球表面有一层均匀和完整的硫酸钡；表面涂覆硫酸钡后的氧化铝空心球具有优畀的抗铝液浸润性能,且其耐压强度明显高于未涂覆的氧化铝空心球.
参考文献
| [1] | 高杰;陈勇;甘明亮 等.氮化硅铁对熔铝炉用高铝质浇注料性能的影响[J].耐火材料,2011,44(增刊):441-445. |
| [2] | 张三华,王战民,胡书禾,李少飞,石会营,曹喜营,喻枫.Al2O3含量及热处理温度对Al2O3-SiO2系浇注料抗铝液侵蚀性的影响[J].耐火材料,2010(01):1-6. |
| [3] | 张艳利 .原位钡长石的形成对铝硅浇注料抗铝液侵蚀性的影响[J].耐火材料,2011,45(05):326. |
| [4] | 王征想,雷其针,周永红.高强度刚玉碳化硅浇注料的研制[J].耐火与石灰,2011(04):15-17. |
| [5] | 李晓娜,陈海,王俊.精炼铝炉用刚玉-镁铝尖晶石复合材料的制备与性能[J].硅酸盐学报,2008(01):49-53. |
| [6] | 张路宁,蔡新宇.THERMBOND浇注料在铝合金熔化炉上的应用[J].耐火材料,2012(03):212-214. |
| [7] | 董童霖,王玺堂,程鹏,占文,周秀坤.发泡法制备莫来石轻质耐火材料工艺研究[J].武汉科技大学学报（自然科学版）,2009(02):184-187. |
| [8] | V. Ya. Sakulin;V. P. Migal;A. P. Margishvili .High-Temperature and Refractory Heat-Insulating Materials Developed at the Borovichi Refractory Kombinat Joint-Stock Co.[J].Refractories and Industrial Ceramics,2004(4):282-288. |
| [9] | Jiabang Wang;Lianbang Wang;Hui Yang .Modification of alumina bubbles with ammonium aluminum sulphate[J].CERAMICS INTERNATIONAL,2006(8):905-909. |
| [10] | Allahevrdi M;Afshar S;Allaire C .Additives and the corrosion resistance of aluminosilicate refractories in molten A1-5 Mg[J].JOM-Journal of the Minerals Metals and Materials Society,1998,50(02):30-34. |
| [11] | Afshar S;Allaire C .Improving low cement castables by non-wetting additives[J].JOM-Journal of the Minerals Metals and Materials Society,2001,53(08):24-27. |
| [12] | M.N. Ibarra Castro;J.M. Almanza Robles;D.A. Cortes Hernandez .The effect of SrSO_4 and BaSO_4 on the corrosion and wetting by molten aluminum alloys of mullite ceramics[J].CERAMICS INTERNATIONAL,2010(4):1205-1210. |
| [13] | M. Oliveira;S. Agathopoulos;J. M. F. Ferreira .The influence of BaO additives on the reaction of Al_2O_3-SiO_2 ceramics with molten Al and Al-Si alloys[J].Acta materialia,2002(6):1441-1451. |
| [14] | Laurent V;Chatain D;Eustathpoulos N .Wettability of SiC by aluminium and Al-Si alloys[J].JMS,1987,22(01):244-250. |
| [15] | 刘有智,李军平,员汝胜,柳来栓.硫酸钡纳米粒子制备方法研究[J].应用基础与工程科学学报,2001(02):141-145. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%