简要介绍了铝熔炼炉的主要类型和冶炼工艺,分析了使用条件,讨论了炉衬耐火材料的使用要求,重点阐述了铝熔炼炉用耐火材料的研究开发和应用情况.
参考文献
| [1] | 熊茹.熔铝炉的炉型与节能[J].轻合金加工技术,2002(05):19-21. |
| [2] | 张锡卿.高效熔铝炉的发展与选择[J].特种铸造及有色合金,1988(3):50-52,55. |
| [3] | Marcel F;Peter van B.Refractories for aluminium cast house industry:melting and holding furnaces[A].Dresden,Germany,2007:424-427. |
| [4] | 陈肇友 .炼铝工业用耐火材料及其发展动向[J].耐火材料,1996,31(1):46-49. |
| [5] | 刘建军;吴海萍 .感应熔铝炉用耐火材料[J].耐火材料,1999,33(5):275-277. |
| [6] | 张三华,王战民,胡书禾,李少飞,石会营,曹喜营,喻枫.Al2O3含量及热处理温度对Al2O3-SiO2系浇注料抗铝液侵蚀性的影响[J].耐火材料,2010(01):1-6. |
| [7] | 宋学斌;罗晨泽;张宝奎 .不污染高纯铝熔液的六铝酸钙基浇注料[P].中国,201010141976.2,2011-10-12. |
| [8] | James G. Hemrick;William L. Headrick;Klaus-Markus Peters .Development and Application of Refractory Materials for Molten Aluminum Applications[J].International journal of applied ceramic technology,2008(3):265-277. |
| [9] | Rana R P;Padhy B P;Bal A S.Processing and characterization of MgAl2O4-calcium aluminate refractories by reaction sintering of alumina-dolomite[A].Victoria,Canada,2013:1153-1158. |
| [10] | 张成行;黄凯;宋明刚 等.微孔高抗渗透高铝浇注料及制备方法和使用方法[P].中国,CN 201210584046,2013-04-03. |
| [11] | 张三华;王战民;曹喜营 等.一种不被铝液润湿的高铝浇注料的制备方法[P].中国,200910227631.6,2012-03-28. |
| [12] | 胡书禾;张三华;王战民 等.一种不被铝液润湿的熔融石英浇注料的制备方法[P].中国,200910227629.9,2012-11-21. |
| [13] | 石会营;王战民;张三华 等.一种不被铝液润湿的高铝可塑料的制备方法[P].中国,200910227630.1,2012-07-11. |
| [14] | 高杰,陈勇,甘明亮,郑小平.氮化硅铁对熔铝炉用高铝质浇注料性能的影响[C].2011全国不定形耐火材料学术会议论文集,2011:441-445. |
| [15] | 陈勇;闰光辉;李友胜 .反润湿剂对熔铝炉用防渗浇注料性能的影响[J].耐火材料,2010,44(增刊):295-297. |
| [16] | Saied A;Claude A .Aluminum resistant refractory composition and method[P].US,US20100216626A1,2010-08-26. |
| [17] | 张路宁,何胜平.铝合金熔化炉熔池内衬刚玉瘤成因及对策[J].耐火材料,2011(06):446-448,451. |
| [18] | 王智斌;于洪娟;马春江 等.50 t熔铝炉炉盖损毁分析及改造实践[J].铝加工,2000,23(6):46-48. |
| [19] | 杨萍.35t熔铝炉炉盖的改造[J].有色设备,2002(01):37-39. |
| [20] | 丛琦;季海堂 .一种浇注料结合预制砖砌筑的铝合金熔化炉保持室炉床[P].中国,200920203760.7,2010-06-23. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%