为了综合利用煤矸石，以煤矸石、滑石等为原料，按堇青石的理论组成配料，分别外加质量分数为0、5％、10％、15％、20％的活性炭粉为造孔剂，在1400℃下分别保温3和6 h烧结后制备了堇青石多孔陶瓷，通过检测显气孔率和常温抗折强度及其显微结构分析探讨了其合成工艺制度。结果表明：利用煤矸石为主原料，外加5％（w）的活性炭为造孔剂，在1400℃下保温6 h可以合成性能优良的堇青石多孔陶瓷。所合成的堇青石多孔陶瓷的抗折强度为29．1 MPa，显气孔率为39．8％；显微结构分析显示，该多孔陶瓷中以堇青石相为骨架，内部形成了贯通气孔的多孔结构。
For comprehensive utilization of coal gangue,porous cordierite ceramics were prepared using coal gangue and talc as starting materials,batching according to the theoretical formulation of cordierite, extra adding activated carbon powder (5%,10%,15%,20%,in mass,respectively)as the pore-forming agent,firing at 1 400℃for 3 h and 6 h,respectively.The apparent porosity,cold modulus of rupture and mi-crostructure were tested to investigate the synthesis process of the ceramics.The results show that the por-ous cordierite ceramics with good performance can be synthesized at 1 400 ℃for 6 h with 5 mass%extra-added activated carbon;the obtained ceramic specimen has cold modulus of rupture of 29.1 MPa and ap-parent porosity of 39.8%.The microscopic structure analysis shows that the skeleton is composed of cordi-erite phase and a porous structure with through pores forms.
参考文献
| [1] | 张振禹;刘蔚玲;耿建刚 .堇青石低热膨胀机理研究[J].地质科学,1997,32(03):308-312. |
| [2] | 赵月明,郭从盛,谭宏斌.堇青石陶资的应用与制备进展[J].中国陶瓷,2011(10):7-9. |
| [3] | 陈玉清;吴皆正 .堇青石的合成及应用[J].中国陶瓷,1992,28(05):38-43. |
| [4] | 饶瑞;孙国才 .堇青石在红外辐射陶瓷材料中的应用[J].中国陶瓷,1998,34(02):39-41. |
| [5] | 刘辉,孙伟,覃文庆,邬顺科.多孔陶瓷材料的应用及发展前景[J].矿冶工程,2003(06):69-71. |
| [6] | Nettleship L.Application of porous ceramics[J].Eng Mater,1996(122-124):305-324. |
| [7] | 刘永杰,孙杰璟,王英姿.堇青石材料的应用[J].山东冶金,2002(03):34-36. |
| [8] | 吴海波,袁波,韩建燊,王刚.多孔陶瓷材料的制备研究进展[J].耐火材料,2012(03):230-235. |
| [9] | 王忠俊,陈永松.煤矸石制备硅铝质高性能陶瓷材料的研究进展[J].中国资源综合利用,2013(01):42-45. |
| [10] | 王辅亚;张惠芬;吴大清 等.堇青石的结构状态与合成温度、热膨胀的关系[J].中国陶瓷,1993,29(02):1-4. |
| [11] | 张华,胡娟,周万城,罗发.堇青石质蜂窝陶瓷的制备[J].硅酸盐学报,2004(01):24-28. |
| [12] | 袁旭暄,贾德昌,周玉.堇青石陶瓷烧结工艺及机理研究[J].陶瓷科学与艺术,2003(06):48-50. |
| [13] | 金文见,周传雄,尹洪峰,梁亚.用煤矸石合成堇青石的工艺研究[J].耐火材料,2005(01):74-75. |
| [14] | Studart, AR;Gonzenbach, UT;Tervoort, E;Gauckler, LJ .Processing routes to macroporous ceramics: A review[J].Journal of the American Ceramic Society,2006(6):1771-1789. |
| [15] | 任强,武秀兰.煤矸石-滑石-菱镁矿低温合成堇青石研究[J].非金属矿,2006(02):29-31. |
| [16] | 张学斌,任祥军,王松林,刘杏芹,孟广耀.堇青石多孔陶瓷的制备与性能表征[J].硅酸盐学报,2006(02):247-250. |
| [17] | 张巍,韩亚苓,潘斌斌.堇青石的合成工艺研究及结构特征[J].陶瓷学报,2008(01):19-23. |
| [18] | 吴庆祝,薛友祥,孟宪谦,江培秋.堇青石质多孔陶瓷高温过滤材料的研究[J].现代技术陶瓷,2003(04):9-12. |
| [19] | 曾令可,李得家,刘艳春,王慧,程小苏,刘平安,税安泽.片状结构堇青石粉体制备的研究[J].人工晶体学报,2009(01):138-142. |
| [20] | 陈留刚,叶国田,翟鹏涛,朱玲玲,张宇翠,傅安平.机械活化含不同镁源的混合物合成堇青石[J].耐火材料,2013(01):14-18. |
| [21] | 林星泵,吴任平,于岩,曾昭望.堇青石质多孔陶瓷的制备及性能研究[J].中国陶瓷,2012(02):49-52. |
| [22] | 张芳,黄志良.利用不同成孔剂制备堇青石质多孔陶瓷[J].武汉工程大学学报,2008(03):69-71. |
| [23] | 杨留栓,汪潇,王宇斌,王继娜,蒋勋.利用煤矸石低温合成堇青石陶瓷粉体的研究[J].硅酸盐通报,2011(06):1391-1394. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%