为了提高泡沫陶瓷浆料的稳定性，进而制备出高孔隙率的泡沫陶瓷，采用没食子酸正丙脂（PG）修饰α-Al2 O3微粉颗粒，使其具有部分疏水性，采用发泡-冷冻干燥法制备了Al2 O3多孔陶瓷材料，主要研究了PG加入量（w，0．1％～2．0％）、料浆固含量（w，49．0％～61．9％）和烧成温度（1300～1500℃）对Al2O3多孔陶瓷材料性能的影响。结果表明：以没食子酸正丙脂（PG）作修饰剂，对α-Al2 O3微粉颗粒稳定气泡有良好的作用；当PG加入量为1．5％（w），固含量为58％（w），烧成温度为1500℃时，制备的Al2 O3多孔陶瓷材料的显气孔率为72％，体积密度为0．59 g·cm-3，耐压强度为12．5 MPa。
To enhance the stabilization of foam ceramic slurries and prepare foam ceramics with high porosi-ty,the porous Al2 O3 ceramics were prepared by foaming-freeze drying method using propyl gallate (PG) modified α-Al2 O3 micropowder with partial hydrophobicity.Effects of PG addition (0.1%-2.0%,in mass, the same hereinafter),slurry solid content (49.0%-61.9%)and firing temperature (1 300-1 500 ℃)on properties of porous Al2 O3 ceramics were researched.The results show that PG modified the α-Al2 O3 mi-cropowder and well stabilizes the pores;when PG addition is 1.5%and solid content is 58%,the apparent porosity,bulk density and crushing strength of the prepared ceramics fired at 1 500 ℃ are 72%,0.59 g·cm -3 and 12.5 MPa,respectively.
参考文献
| [1] | 吴海波,袁波,韩建燊,王刚.多孔陶瓷材料的制备研究进展[J].耐火材料,2012(03):230-235. |
| [2] | 曹贺辉,王刚,袁波,韩建燊,董宾宾.泡沫注凝法制备刚玉-莫来石多孔陶瓷[J].耐火材料,2013(05):334-337. |
| [3] | 徐鲲濠,孙阳,黄勇,孙加林.叔丁醇基凝胶注模成型制备氧化铝多孔陶瓷[J].耐火材料,2011(02):93-95,99. |
| [4] | Gonzenbach U T;Gauckler L J;Studart A R et al.Ulstrastable parti-cle-stabilized forms[J].Angew Chen Int Ed,2006,45(21):3526-3530. |
| [5] | Urs T. Gonzenbach;Andre R. Studart;Elena Tervoort .Macroporous Ceramics from Particle-Stabilized Wet Foams[J].Journal of the American Ceramic Society,2007(1):16-22. |
| [6] | Pugh R J;Bergstrom L.Surface and colloid chemistry in advanced ce-ramic processing[M].New York:MarcellDekkler Inc,1994:193-196. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%