为降低镁质浇注料的原料成本，用镁橄榄石骨料部分替换镁质浇注料中等粒度的镁砂骨料，研究了镁橄榄石加入量（加入质量分数分别为0、16％、32％）对不同温度（110、1000和1500℃）处理后浇注料性能的影响。结果表明：随着镁橄榄石加入量的增大，浇注料烘干后体积密度减小，显气孔率变小，强度增大；1000和1500℃热处理后，浇注料体积密度减小，显气孔率增大，强度增大，抗渣侵蚀性降低，抗渣渗透性以镁橄榄石加入量为16％（w）时最好。
Effect of forsterite addition (0,16% and 32%,in mass,the same hereinafter)on properties of castables treated at different temperatures (1 10,1 000 and 1 500 ℃)were researched using forsterite ag-gregate to partially substitute medium particle size magnesia aggregate in MgO castables in order to cut the cost.The results show that with forsterite addition increasing,for the castables after drying,the bulk density and apparent porosity decrease,the strength increases;after fired at 1 000 and 1 500 ℃,the bulk density and slag corrosion resistance decrease,apparent porosity and strength increase,when forsterite addition is 16%,the castables perform the best slag penetration resistance.
参考文献
| [1] | 李志刚,叶方保,钟香崇.锆英石和氧化铝加入量对镁质浇注料性能的影响[J].耐火材料,2001(06):320-322. |
| [2] | 毕振勇;周宁生;钟香崇 .氧化镁-尖晶石浇注料的组成与性能的关系[J].耐火材料,1999,33(01):12-15. |
| [3] | 张三华;毕振勇;周宁生 等.钢包渣线用MgO-尖晶石-Cr2 O3 浇注料的研制与应用[J].耐火材料,1999,33(03):150-153. |
| [4] | 李友胜,李楠,王英东.MgO-Al2O3-TiO2浇注料的组成、结构及性能[J].耐火材料,2002(02):86-87. |
| [5] | 涂军波,魏军从,崔博.氮化硅铁加入量对镁质浇注料力学性能的影响[J].硅酸盐通报,2009(06):1149-1153. |
| [6] | 丁军,邓承继,祝洪喜,员文杰,张小军.以Na2SO4介质制备镁橄榄石轻质材料的性能研究[J].耐火材料,2013(05):358-361. |
| [7] | 陈勇,于景坤,甘明亮.镁橄榄石对中间包镁质干式料性能的影响[J].耐火材料,2012(01):28-30. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%