为了降低Al2 O3多孔陶瓷制备过程中的干燥后收缩和烧后收缩，提高成品率，将d50分别为25．1、9．4和1．1μm的粗、中、细Al2 O3粉体按粗粉中粉细粉质量比分别为504010、104050和100％全细粉的级配方式制备Al2 O3泡沫浆料，研究颗粒级配对浆料黏度、干燥生坯的线收缩、烧后试样的线收缩、烧后试样的热导率等性能的影响。结果表明：颗粒级配可以有效提高固含量，且颗粒级配后的发泡浆料在静置30 min后仍能保持稳定，颗粒级配可以明显降低生坯的干燥线收缩以及烧后线收缩，并能降低热导率，提高了发泡法-凝胶注模工艺制备氧化铝多孔陶瓷的成品率。
Al2 O3 foam slurries were prepared according to 50 40 10 and 10 40 50 of mass ratio of coarse powder (d50 =25.1 μm)medium powder (d50 =9.4 μm)fine powder (d50 =1.1 μm),and 100%fine pow-ders,respectively,in order to reduce drying shrinkage and sintering shrinkage and enhance the rate of final products of porous Al2 O3 ceramics.Effects of particle size distribution on slurry viscosity,linear shrinkage of dried green bodies,linear shrinkage and thermal conductivity of sintered bodies were researched.The re-sults show that adjusting particle size distribution can increase the solid content effectively,keep the foam slurries stable within 30 min,significantly lower the linear shrinkage of the dried green bodies and sintered bodies and thermal conductivity,and increase the rate of final products of porous Al2 O3 ceramics.
参考文献
| [1] | 刘培生.多孔材料导论[M].北京:清华大学出版社,2005:1-3. |
| [2] | 吴海波,袁波,韩建燊,王刚.多孔陶瓷材料的制备研究进展[J].耐火材料,2012(03):230-235. |
| [3] | 于洪浩.陶瓷凝胶注模成型技术及其应用研究[J].辽宁化工,2007(04):260-262,265. |
| [4] | 曹贺辉,王刚,袁波,韩建燊,董宾宾.泡沫注凝法制备刚玉-莫来石多孔陶瓷[J].耐火材料,2013(05):334-337. |
| [5] | 刘开琪,宋慎泰,洪彦若,孙加林.凝胶注模成型工艺的研究进展[J].耐火材料,2004(05):343-346. |
| [6] | 吴海波,袁波,韩建燊,王刚.凝胶注模常温发泡制备氧化铝多孔陶瓷[J].材料科学与工艺,2012(04):144-148. |
| [7] | 徐鲲濠,孙阳,黄勇,孙加林.叔丁醇基凝胶注模成型制备氧化铝多孔陶瓷[J].耐火材料,2011(02):93-95,99. |
| [8] | 刘炜;杨金龙;董英鸽 等.颗粒级配对凝胶注模成型氧化铝陶瓷的影响[J].人工晶体学报,2009,38(增刊):211-214. |
| [9] | 尚阿曼,梁迎春,冯佳伦,张巨先.粉体颗粒级配对多孔Al2O3陶瓷性能的影响[J].真空电子技术,2012(04):37-40. |
| [10] | 申轶男,陈华辉,胡宇.原料颗粒级配对多孔陶瓷性能的影响[J].材料研究学报,2011(05):550-556. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%