为了提高MgO-CaO 耐火材料的抗水化性能，在白云石粉（≤0．0374 mm）掺加10％（w）的石英粉（≤0．045 mm）合成MgO-CaO-SiO2耐火材料，并着重探究了煅烧温度分别为1400、1500、1600、1650℃时对MgO-CaO-SiO2耐火材料致密性及抗水化性能的影响。结果表明：随着煅烧温度的升高，试样的致密度增大，抗水化性增强，但煅烧温度达到1650℃时出现过烧现象；在煅烧过程中，SiO2与CaO反应生成了3CaO·SiO2，但仍有游离态CaO存在，可净化钢液。
MgO-CaO-SiO2 refractories were synthesized by doping 10 mass% quartz powders (≤0.045 mm)into dolomite powders(≤0.037 4 mm)to improve the hydration resistance of MgO-CaO refractories. The influence of calcination temperatures (1 400,1 500,1 600 and 1 650 ℃ )on density and hydration re-sistance of MgO-CaO-SiO2 refractories was researched.The results show that:with the calcination temper-ature rising,the density of specimens increases,the hydration resistance strengthens,while the specimen is over burned at 1 650 ℃;SiO2 reacts with CaO forming 3CaO·SiO2 during calcination,but there still exists free CaO which can purify the molten steel.
参考文献
| [1] | 王宏联,崔庆阳,薛群虎,闫振华,宋鹏涛,田晓丽.MgO-CaO耐火材料性能研究进展[J].耐火材料,2010(01):67-70,74. |
| [2] | 高心魁.镁钙系耐火材料在炉外精炼炉上的应用[J].耐火材料,2012(01):9-13. |
| [3] | Chen Min;Cai yun;Yu Jingkun .Improvement in performance of MgO-CaO refractories by addition of nano-sized ZrO2[J].Journal of the European Ceramic Society,2004,27(16):4633-4638. |
| [4] | G. I. Antonov;V. P. Nedosvitii;A. S. Kulik .STABILIZED DOLOMITE REFRACTORIES[J].Refractories and Industrial Ceramics,2004(3):160-164. |
| [5] | 张寒,赵惠忠,陈金凤,余俊,聂建华.掺CeO2的MgO-CaO材料缺陷研究[J].功能材料,2013(16):2343-2347. |
| [6] | Otroj S;Nilforoushan M R .不同结合剂对白云石砖性能的影响[J].耐火材料,2007,41(增刊):132-134. |
| [7] | S. OTROJ,M. R. NILFOROUSHAN.Influence Parameters on Properties of Dolomite Bricks Containing Different Bonding Systems[J].中国耐火材料（英文版）,2007(04):8-10. |
| [8] | 朱秀英;孙钦英;廖闯新 .锆英石加入物对MgO-CaO系材料结构与性能的影响[J].耐火材料,1995,29(06):317-323. |
| [9] | Antonov G I;Nedosvitii V P;Semenenko O M .Laboratory study of the technology of stabilized dolomite products[J].Refract Ind Ce-ram,1997,38(04):154-157. |
| [10] | 陶博,赵惠忠,余俊,聂建华.制备工艺因素对镁白云石性能的影响[J].材料工程,2010(z2):241-245. |
| [11] | 罗明,李楠,郑海忠,邱文冬.外加剂对白云石烧结及抗水化性的影响[J].耐火材料,2001(01):14-15,18. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%