按照ZrB2和SiC的质量比为7525配料，混料、烘干、热压烧结后，经线切割加工成ZrB2－SiC复合陶瓷直型发热体，研究了发热体的物相组成、微观形貌及在空气和氩气气氛下发热温度随电流电压的变化规律。结果表明，ZrB2－SiC复合陶瓷由均匀分布在ZrB2基体晶界处的SiC颗粒和尺寸小于10μm的等轴状基体ZrB2颗粒组成；在空气和氩气气氛下，ZrB2－SiC复合陶瓷发热体的温度均随电流、电压及加热时间的延长呈稳步增大趋势，同时空气气氛下发热体的电阻随温度升高而增大，并呈现线性变化；在空气和氩气气氛下，ZrB2－SiC复合陶瓷发热体表面温度分别达到1800和2200℃。同时，与铬酸镧和氧化锆发热体相比，其电压、电阻变化较小，电流较大。
ZrB2-SiC composite ceramic straight heating elements were prepared using ZrB2 and SiC as starting materials (the mass ratio of ZrB2 SiC=75 25),mixing,drying,hot pressing sintering,and then lin-ear cutting.The phase compositions and microstructure of the heating elements,and the change of heating temperature with current and voltage in air and Ar atmosphere were researched.The results show that:(1) ZrB2-SiC composite ceramics are composed of SiC grains (well distributed around the crystal boundaries of ZrB2)and the equant ZrB2 grains (<10 μm);temperature of the heating element rises gradually with voltage and electric current increasing and heating period prolonging in air and Ar atmosphere.Mean-while,in air,the heating element resistance increases with temperature rising linearly;in air and Ar atmos-phere,the surface temperatures of the heating elements reach 1 800 and 2 200 ℃,respectively.Compared with the chromate lanthanum and zirconia heating elements,the voltage and resistance change of the de-veloped ones are smaller and the current change is larger.
参考文献
| [1] | 江东亮;李龙土;欧阳世翕.无机非金属材料手册(上)[M].北京:化学工业出版社,2009:202-203. |
| [2] | Hailong Wang;Chang-An Wang .Processing and Mechanical Properties of Zirconium Diboride-Based Ceramics Prepared by Spark Plasma Sintering[J].Journal of the American Ceramic Society,2007(7):1992-1997. |
| [3] | Rong TU;Hideroni HIRAYAMA;Takashi GOTO .Preparation of ZrB2-SiC composites by arc melting and their properties[J].日本セラミックス协会学术论文志,2008(1351):431-435. |
| [4] | William G. Fahrenholtz;Gregory E. Hilmas;Inna G. Talmy;James A. Zaykoski .Refractory Diborides of Zirconium and Hafnium[J].Journal of the American Ceramic Society,2007(5):1347-1364. |
| [5] | Rezaie A;Fahrenholtz WG;Hilmas GE .Effect of hot pressing time and temperature on the microstructure and mechanical properties of ZrB2-SiC[J].Journal of Materials Science,2007(8):2735-2744. |
| [6] | 周森安;郑传涛;李小华 等.一种二硼化锆复合陶瓷材料发热元件[P].中国,201020125478.4,2011 -08-24. |
| [7] | Monteverde F.;Guicciardi S.;Bellosi A. .Advances in microstructure and mechanical properties of zirconium diboride based ceramics[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):310-319. |
| [8] | 胡宝玉;徐延庆;张宏达.特种耐火材料使用手册[M].北京:冶金工业出版社,2004:391-395. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%