为了进一步提高酸洗后铝铬渣烧结块的性能尤其是其抗热震性，取粒度≤0．045 mm的铝铬渣，在浓盐酸中煮沸20 min后，过滤，洗净，干燥，制成酸洗铝铬渣。在酸洗铝铬渣中分别加入4％（w）的钛白粉、锆英石粉或钛白粉－锆英石粉复合粉（钛白粉与锆英石粉的质量比为11），经混练、成型、干燥后，在1500℃保温2 h热处理制成烧结铝铬渣试样，然后检测其体积密度、显气孔率、常温耐压强度、常温抗折强度和抗热震性，并分析其显微结构。结果表明：在酸洗铝铬渣中分别添加钛白粉、锆英石粉或复合添加钛白粉－锆英石粉均可提高烧结铝铬渣试样的致密度、常温强度和抗热震性，其中，添加钛白粉－锆英石粉试样的综合性能提高幅度最大。
The acid washed alumina chrome slag was prepared using ≤0.045 mm alumina chrome slag, boiling in concentrated hydrochloric acid for 20 min,filtrating,washing,and drying to enhance the proper-ties,especially the thermal shock resistance.Then 4 mass% of TiO2,ZrO2 or TiO2 +ZrO2 (mass ratio of TiO2 ZrO2 =1 1)was added into the treated slag,respectively,mixing,shaping,drying,and firing at 1 500℃ for 2 h.The bulk density,apparent porosity,cold crushing strength,cold modulus of rupture and thermal shock resistance were analyzed,and the microstructure was observed.The results show that adding TiO2, ZrO2 or TiO2 +ZrO2 separately can improve the density,cold strength and thermal shock resistance,and the specimens with TiO2 +ZrO2 perform the best properties.
参考文献
| [1] | 刘帅,朱逾倩,宋建义,杨柏,于童,曹杨.铝铬渣在耐火材料上的应用与开发[C].第十三届全国耐火材料青年学术报告会暨2012年六省市金属(冶金)学会耐火材料学术交流会论文集,2012:554-555. |
| [2] | 刘帅,侯庆东,刘森起.碳素铬渣用于耐火材料的探讨[J].耐火材料,2010(04):317-318. |
| [3] | 曹杨,郑丽君,宋建义.镁砂加入量及粒度对铬渣砖性能的影响[J].耐火材料,2013(05):396,399. |
| [4] | 郑丽君,张国栋,曹杨,刘峰.利用铝铬渣与废弃镁碳砖合成镁铝尖晶石材料[J].硅酸盐通报,2013(08):1506-1509,1514. |
| [5] | 罗旭东,张国栋,曲殿利,刘海啸.氧化铬及铝铬渣对镁铝浇注料性能的影响[C].第十三届全国耐火材料青年学术报告会暨2012年六省市金属(冶金)学会耐火材料学术交流会论文集,2012:116-120. |
| [6] | 陈花朵,王长春.添加铝铬渣的钢包水口座砖的研制和应用[J].耐火材料,2013(05):374-376. |
| [7] | 郑丽君;张国栋;曲殿利 等.铝铬渣酸洗时间对其烧结体材料性能的影响[J].耐火材料,2013,47(增刊2):398-399. |
| [8] | 徐刚,韩高荣.钛酸铝材料的结构、热膨胀及热稳定性[J].材料导报,2003(12):44-47. |
| [9] | 闫洪,窦明民,李和平.二氧化锆陶瓷的相变增韧机理和应用[J].陶瓷学报,2000(01):46-50. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%