为了优化纯铝酸钙水泥结合刚玉－尖晶石浇注料的性能，分别用6～3、3～1和1～0．5 mm 的六铝酸钙（CA6）颗粒替代浇注料中相应粒度的板状刚玉颗粒，研究其对浇注料强度、致密度、烧后线变化和抗热震性的影响。结果表明：1）用 CA6颗粒替代板状刚玉颗粒后，试样的常温强度、高温强度、抗热震性、1550℃烧后线变化均增大，并且其增大幅度基本上随 CA6颗粒粒度的减小而增大。2）用6～3 mm 的 CA6颗粒替代板状刚玉颗粒，试样的体积密度减小，显气孔率增大；但随着 CA6颗粒粒度从6～3 mm 逐渐减小至1～0．5 mm，试样的体积密度逐渐增大，显气孔率逐渐减小。
Calcium hexaluminate aggregates (CA6 ,6 -3,3 -1 and 1 -0.5 mm)were used to replace the tabular corundum aggregates with corresponding particle size in corundum-spinel castables in order to optimize the performance of the castables.Effects of calcium hexaluminate aggregates on the strength, density,linear change on heating (1 550 ℃)and thermal shock resistance of the castables were studied. The results show that:after replacement,(1)the cold strength,hot strength,thermal shock resistance and linear change on heating increase,and the increasing amplitude basically increases with the decrease of calcium hexaluminate particle size;(2)for the castables with 6 -3 mm CA6 aggregates,the bulk density de-creases and the apparent porosity increases,however,as CA6 decreases from 6 -3 mm to 1 -0.5 mm,the bulk density increases and the apparent porosity decreases gradually.
参考文献
| [1] | 岳卫东,聂洪波,李继伟,陈挺举,陈许周.大型精炼钢包用刚玉-尖晶石质透气砖的研制与使用[J].耐火材料,2005(06):442-444. |
| [2] | 朱伯铨,祝洪喜,蒋春华,帅汉舟.RH插入管刚玉-尖晶石浇注料研制与应用[J].炼钢,2000(01):20-22. |
| [3] | 张启东,潘洪涛,余西平,宋林喜.LF精炼钢包用铝尖晶石浇注料的研制与应用[J].耐火材料,2001(06):340-341. |
| [4] | 顾华志,汪厚植,张文杰,马金光,张平宣.连铸钢包用高纯铝镁系浇注料的性能与损毁[J].钢铁研究,2002(02):6-8,36. |
| [5] | 程瑛,张立明,马兆宏,黄辉.用后钢包透气砖显微结构分析[J].耐火材料,2008(01):54-57. |
| [6] | Khalil N M .Heat resistance and thermomechanical behavior of ultra-low and zero cement castables[J].British Ceramic Transactions,2004,103(01):37-41. |
| [7] | 李有奇,李亚伟,金胜利,李楠.六铝酸钙材料的合成及其显微结构研究[J].耐火材料,2004(05):318-323. |
| [8] | A.J. Sanchez-Herencia;R. Moreno, C. Baudin .Fracture behaviour of alumina-calcium hexaluminate composites obtained by colloidal processing[J].Journal of the European Ceramic Society,2000(14/15):2575-2583. |
| [9] | 刘新彧,Andreas Buhr,Gunter Büchel,R P Racher.博耐特（Bonite）--一种新型的合成致密CA6耐火原料[J].耐火材料,2006(01):60-64. |
| [10] | Criado E .CA6 耐火材料[J].国外耐火材料,1992,17(10):58-63. |
| [11] | 龙斌;周云鹏;田忠凯.高性能六铝酸钙耐材原料[A].太原,中国,2014:173-181. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%