利用应变电测法测量了致密耐火浇注料在单面快速烘烤过程中其内部应力的变化。结果表明：1）在快速烘烤过程中，靠近受热面的位置承受压应力，距离受热面越近压应力越大。2）在快速烘烤过程中试样发生了爆裂。3）在对爆裂时结构产生的应力计算后发现，与爆裂面同深度位置产生的压应力超过了结构的强度极限。
The change of the internal stress of dense refractory castables during unilateral rapid heating was studied by the electric stress measurement.The results indicate that:(1)during rapid heating,the position near the heated surface is under compressive stress;the closer the position to the heated surface,the lar-ger the compressive stress;(2)the specimen bursts during the rapid heating;(3)the calculated stress of the structure at the burst moment shows that the compressive stress produced at the same depth as the cracking surface exceeds the ultimate strength of the structure.
参考文献
| [1] | 谢长清.高技术浇注料施工及防爆裂研究与应用[J].四川冶金,2003(02):26-29,25. |
| [2] | 申向利.低水泥浇注料抗爆裂性能的改善[J].建材技术与应用,2003(04):3-5. |
| [3] | 赵瑾;王战民;曹喜营.耐火浇注料透气性研究现状[J].耐火材料,2014(2):149-154. |
| [4] | 朱珠;王战民;曹喜营;黄育飞;赵瑾.刚玉质浇注料加热过程中内部不同位置的蒸汽压力和温度[J].耐火材料,2013(5):338-340. |
| [5] | 王卫华;解家英;王凤琴;张延平;李占营;张艳萍.方坯在加热炉升温过程中的热应力分析[J].中国制造业信息化,2008(24):88-91. |
| [6] | 王绪东;薛乃彦;梅鸣华;褚晓彦.高温热应变测试技术及其在耐火浇注料上的应用[J].金属学报,2000(4):438-440. |
| [7] | 王绪东,薛乃彦,梅鸣华,褚晓彦.耐火浇注料预制件热应变测试的研究[C].国际耐火材料学术会议论文集（第三届国际耐火材料学术会议）,1998:298~303. |
| [8] | 管东芝;邢晨曦;韩苏闽.电测法应用于混凝土结构的表面应变测试[J].实验室研究与探索,2011(1):30-32. |
| [9] | 张彦兵;陈树礼;冯小利.几种常用应变测试技术的比较分析[J].山西建筑,2006(3):77-78. |
| [10] | 李艳;李新娥;裴东兴.应变测量系统误差分析[J].现代电子技术,2008(24):181-183. |
| [11] | 张富生 .应变—温度法监测钢轨无缝线路锁定轨温的误差分析及改进[D].大连理工大学,2013. |
| [12] | 亢景付;赵蒙蒙;蒋元成;荆锐.约束程度与温度应力之间的关系研究[J].水利与建筑工程学报,2014(6):21-25. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%