以板状刚玉、铝酸钙水泥、氧化铝微粉和电熔尖晶石细粉（AM70、AM85、AM90）为主要原料，设计了三组 MgO 含量均为1．4％（w）、含不同组成尖晶石的刚玉－尖晶石浇注料，分别经1500℃保温5 h 和1650℃保温5 h 热处理后，研究了尖晶石组成对刚玉－尖晶石浇注料显微结构的影响。结果表明：在热处理过程中，AM70尖晶石与其周围刚玉相发生固溶反应，使尖晶石和刚玉烧结在一起，浇注料中尖晶石、CA6相通过刚玉相以多种结合方式联结；AM85和 AM90尖晶石发生脱溶析出刚玉相，刚玉相再与周围水泥在尖晶石颗粒边缘反应生成 CA6，形成尖晶石－CA6结合，浇注料中尖晶石和刚玉通过 CA6联结。
Three groups of corundum-spinel castables with 1.4 mass% MgO and different grades of spinels were designed using tabular corundum,calcium aluminate cement,reactive alumina and fused spinel fines (AM70,AM85,AM90)as main materials.After heat treatment at 1 500 ℃ for 5 h and 1 650 ℃ for 5 h,effect of spinel grade on microstructure of corundum-spinel castables was investigated.The results show that:during heat treatment,AM70 spinels solid solve the surrounding corundum phases,combining them togeth-er;the spinels combine with CA6 through corundum by various styles;exsolution and precipitation of corun-dum phase occur in AM85 or AM90 spinels,and corundum reacts with the surrounding cement forming CA6 on the edges of spinels particles,and then forming spinel-CA6 combination,the spinels and corundum in the castables are combined by CA6 .
参考文献
| [1] | 韩斌;王会先;赵世杰;寇志奇;禄向阳;张晖.尖晶石粒度对高纯刚玉-尖晶石浇注料性能的影响[J].耐火材料,2002(4):187-189. |
| [2] | 王辉;崔庆阳.尖晶石对刚玉-尖晶石浇注料性能的影响[J].河南冶金,2011(5):14-16. |
| [3] | 张志雄,李志刚,张立明.骨料和细粉对刚玉-尖晶石浇注料抗热震性能的影响[C].2009全国不定形耐火材料学术会议论文集,2009:108-113. |
| [4] | 贾全利,叶方保,钟香崇.CaO含量对刚玉-尖晶石浇注料性能的影响[C].第十二届全国耐火材料青年学术报告会论文集,2010:168-171. |
| [5] | 姚金甫;张恩甫;田守信.α-Al2O3微粉对刚玉-尖晶石浇注料性能的影响[J].耐火材料,2008(3):209-211. |
| [6] | E.Y. Sako;M.A.L. Braulio;V.C. Pandolfelli.The corrosion resistance of microsilica-containing Al_2O_3-MgO and Al_2O_3-spinel castables[J].CERAMICS INTERNATIONAL,20126(6):4783-4789. |
| [7] | Emre Yalamac;Claude Carry;Sedat Akkurt.Microstructural development of interface layers between co-sintered alumina and spinel compacts[J].Journal of the European Ceramic Society,20119(9):1649-1659. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%