为了研究菱镁矿在不同温度轻烧后的显微结构与活性，取粒度＜0．074 mm 的菱镁矿粉分别在850、900、950、1000、1050、1100、1150和1200℃保温2 h 煅烧制备了轻烧镁粉。采用柠檬酸溶解－EDTA 络合滴定法测定了试样中活性氧化镁的含量，并利用 XRD 和 SEM对试样的物相组成和显微结构进行了分析。结果表明：在850～1050℃阶段，方镁石的晶粒尺寸增加缓慢，其活性氧化镁含量变化并不明显，均高于80％（w）；在1050～1200℃阶段，方镁石的晶粒尺寸快速增加，其活性氧化镁含量快速降低。
In order to study the microstructure and activity of magnesite calcined at different temperatures, the magnesite powder (<0.074 mm)was calcined at 850,900,950,1 000,1 050,1 100,and 1 200 ℃ for 2 h, respectively.The active magnesia content in specimens was determined by citric acid-EDTA complexo-metric titration method,and the phase composition and microstructure of specimens were characterized by XRD and SEM.The results show that,at 850 -1 050 ℃,the grain size of periclase increases slowly,the ac-tive magnesia content changes unobviously (higher than 80 mass%);at 1 050 -1 200 ℃,the grain size of periclase increases rapidly,and the active magnesia content reduces quickly.
参考文献
| [1] | 王兆敏.中国菱镁矿现状与发展趋势[J].中国非金属矿工业导刊,2006(05):6-8,23. |
| [2] | 张永奎.我国菱镁矿的开发利用现状及前景分析[J].科技信息,2013(5):424-425. |
| [3] | 钱海燕;邓敏;徐玲玲;张少明.轻烧氧化镁活性测定方法的研究[J].化工矿物与加工,2005(1):22-24,35. |
| [4] | 李广垠,郭玉香,徐娜,蔡幼娟,李志坚.利用柠檬酸溶解-EDTA络合滴定法定量分析轻烧镁砂中活性MgO初探[C].2015耐火材料综合学术年会暨第十三届全国不定形耐火材料学术会议、2015耐火原料学术交流会论文集,2015:696-697. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%