研究了硼氢化钾、次磷酸钠、热碱溶液处理等表面处理方法对镧镨铈(LPC)贮氢合金电极电化学性能影响.结果表明,在研究范围内,各种表面处理方法均明显改善电极的活化性能,提高初始放电容量;热碱处理的时间和温度对电化学性能影响很大;KBH4处理能明显改善循环稳定性,但降低最大容量;NaH2PO4处理能提高最大放电容量,但不利于循环稳定性的提高;综合比较,热碱处理的综合电化学性能最好,且工艺简单,成本低廉.
参考文献
| [1] | Sakai T;Ishikawa H;Ogure K et al.Effect of microencapsulation of hydrogen storage alloy on the performances of sealed nickel/ metal hydride batteries[J].Journal of the Electrochemical Society,1987,134:558-562. |
| [2] | Zhang Y;Chen Y, Y S et al.Accumulation of rare-earth metal on the surface of the microencapsulated hydrogen storage alloy[J].Journal of Alloys and Compounds,1993,190:L37-L38. |
| [3] | Sakai T H;Hazama T;Miyamura H.rate-earth-based alloy electrodes for a nickel-metal hydride battery[J].Journal of the Less-Common Metals,1991:172-174:1175-1184. |
| [4] | 朱建新,于波.利用表面修饰提高AB5型贮氢电极性能[J].表面技术,2001(05):64-67. |
| [5] | 孙俊才;雷永泉;吴京 等.微型包覆处理稀土贮氢合金电极的循环稳定性[J].材料科学与工艺,1995,3(01):49-52. |
| [6] | 傅静媛.酸化处理对MmNi3.45Co0.75Mn0.6Al0.2贮氢合金性质的影响[J].金属功能材料,1998(06):268. |
| [7] | Matsuoka M;Asai K;Fukumoto Y et al.Surface modification of hydrogen storage alloy electrode with an alkaline solution contain ing potassium borohyclride as a reducing agent[J].Electrochimica Acta,1993,38:659-662. |
| [8] | Yan D Y;Sandrock G;Suda S .Activation of Zro.5Ti0.5 Vo.75 Ni.25 alloy electrodes by hot alkalinesolufions[J].Journal of Alloys and Compounds,1994,216:237-242. |
| [9] | 唐定骧;王成辉 .镧镨铈新型混合稀土金属及其生产工艺[P].CN:1239152B |
| [10] | 涂铭旌;陈云贵;李全安 等.镧镨铈-镍系贮氢合金电极材料[P].CN:1252627A |
| [11] | 李全安 .LPC贮氢合金电极材料的研究与开发[D].四川大学,2000. |
| [12] | 李全安,桑革,李建文,陈云贵,涂铭旌.非化学计量比贮氢合金及其电极特性[J].功能材料,2001(02):156-157,163. |
| [13] | 大角泰章.贮氢合金[J].国外金属加工,1995(03):29-37. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%