采用多层结构的方法可以提高TiN刀具涂层力学性能和切削性能.采用离子镀技术制备了TiN(0.5μm)/Ti(CN)(0.5μm)/TiN(0.5μm)多层涂层.利用光学显微镜、原子力显微镜和微力学探针表征了涂层的微结构和力学性能,并研究了涂层对硬质合金铣刀切削性能的影响.结果表明,TiN/Ti(CN)多层涂层表面平整、厚度均匀、与基底结合良好,硬度为28.5GPa.高速干式切削试验表明,与普通硬质合金铣刀相比,涂层铣刀的使用寿命提高5倍.
参考文献
| [1] | 田明波;刘德令.薄膜科学与技术手册[M].北京:机械工业出版社,1991 |
| [2] | PalDey S.;Deevi SC. .Single layer and multilayer wear resistant coatings of (Ti,Al)N: a review [Review][J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):58-79. |
| [3] | P.C. Jindal;A.T. Santhanam .Performance of PVD TiN, TiCN, and TiAlN coated cemented carbide tools in turning[J].International Journal of Refractory Metals & Hard Materials,1999(1/3):163-170. |
| [4] | 田家万,韩增虎,赖倩茜,戴嘉维,李戈扬.硬质涂层力学性能可靠测量的两步压入法[J].功能材料,2002(04):384-386. |
| [5] | Oliver W C;Pharr G M .An improved technique for deter mining hardness and elastic modulus using load and displacement sensing indentat ion experiments[J].Journal of Materials Research,1992,7(06):1564-1583. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%