使用AC-HVAF喷涂工艺分别制备了纳米和微米结构的高铬镍基合金涂层,对两种涂层和20G钢在550℃和650℃表面涂盐情况下的热腐蚀性能进行了研究,并利用配有能谱分析仪的扫描电镜(SEM)和X-ray衍射仪(XRD)对涂层腐蚀产物的形貌、成分和相组成进行了分析.试验结果表明,腐蚀后的两种涂层表面均生成一层连续致密的氧化铬保护膜,可有效抑制腐蚀反应的进程.在相同腐蚀条件下,纳米结构涂层比微米结构涂层具有更低的腐蚀增重,显示出更优异的抗热腐蚀性能.
参考文献
| [1] | 徐滨士,马世宁,李长青.几种电弧喷涂涂层抗热腐蚀性能研究[J].中国表面工程,1998(02):14. |
| [2] | 樊自拴,孙冬柏,俞宏英,李辉勤,孟惠民,张济山,乔力杰.超音速火焰喷涂技术研究进展[J].材料保护,2004(09):33-35. |
| [3] | Wang F .Oxidation resistance of sputtered Ni3 (AlCr) nanocrystalline coating[J].Oxidation of Metals,1997,47(03):247-258. |
| [4] | Myung J S;Lim H J;Kang S G .Oxidation behavior of nanocrystalline Al alloys containing 5 and 10 at% Ti[J].Oxidation of Metals,1999,51(01):79-95. |
| [5] | Geng S;Wang F;Zhu S et al.Hot-corrosion resistance of a sputtered K38G nanocrystalline coating in molten sulfate at 900℃[J].Oxidation of Metals,2002,51(05):549-557. |
| [6] | Lima RS;Marple BR .From APS to HVOF spraying of conventional and nanostructured titania feedstock powders: a study on the enhancement of the mechanical properties[J].Surface & Coatings Technology,2006(11):3428-3437. |
| [7] | JI Gang,高泰瑞,郝胜智,LIAO Hanlin,董闯.HVOF喷涂成形纳米晶FeAl厚涂层的结构和热稳定性[J].金属学报,2005(06):561-567. |
| [8] | 朱日彰;何业东;齐慧滨.高温腐蚀及耐高温腐蚀材料[M].上海:上海科学技术出版社,1995:262. |
| [9] | 张允书;李选明;史良权 等.K2SO4-Na2SO4沉积引起的Fe-Cr合金的低温热腐蚀[J].中国腐蚀与防护学报,1991,11(01):18-26. |
| [10] | 李铁藩.金属晶界在高温氧化中的作用[J].中国腐蚀与防护学报,2002(03):180-183. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%