研制了新型Mg-Hg-X合金阳极材料,用扫描电镜(SEM)、能谱、X-射线衍射(XRD)和电化学测试等方法分析了镁合金阳极材料在海水介质中腐蚀前后的微观结构、表面形貌及表面元素的组成,研究了Mg-Hg-X合金阳极的溶解过程及活化机理.结果表明:在放电初期,Mg-Hg-X合金阳极材料中的第2相粒子随点腐蚀的发生直接脱落,形成腐蚀坑,随后Mg-Hg-X合金阳极溶解在介质中的合金元素离子与基体镁发生反应,再沉积于镁阳极材料表面的点蚀孔中,形成Hg、X的沉积层,破坏钝化膜的结构,降低了Mg-Hg-X合金阳极极化.使电极电位负移,同时沉积的具有高析氢过电位的Hg、X抑制了析氢腐蚀.
参考文献
| [1] | E. D. Morales;E. Ghali;N. Hort .Corrosion Behaviour of Magnesium Alloys with RE Additions in Sodium Chloride Solutions[J].Materials Science Forum,2003(Pt.2):867-872. |
| [2] | Udhayan R;Muniyandi N;Mathur P B .Studies on magnesium and its alloys in battery electrolytes[J].British Corrosion Journal,1992,27(01):68-71. |
| [3] | Carmel B Breslin;William M Carroll .The effects of indium precipitates on the electrochemical dissolution of Al-In alloys[J].Corrosion Science,1993,34(07):1099-1109. |
| [4] | Muniyandi N;Vasudevan S;Pitehumani S .Performance characteristics of chloro-substituted dinitrobenzene for magnesium reserve batteries[J].Power Sources,1993,45(02):119-130. |
| [5] | 王树宗 .鱼雷动力电池技术发展水平概述[J].海军工程学院学报,1994,14(01):66-70. |
| [6] | 龚金保.不同温度下AZ41镁基合金牺牲阳极的电化学行为[J].腐蚀科学与防护技术,1997(01):23. |
| [7] | 曾爱平;张承典;徐乃欣 .淡水中镁基牺牲阳极上的析氢行为[J].中国腐蚀与防护学报,1999,19(02):85-90. |
| [8] | 张信义.合金元素对Al-Zn-In-Ca合金牺牲阳极性能的影响[J].材料保护,1996(02):3. |
| [9] | 吴益华 .合金元素在铝基牺牲阳极活化过程中的作用[J].中国腐蚀与防护学报,1989,9(02):113-120. |
| [10] | 龚金保;徐乃欣;张承典 .交流电干扰对镁合金AZ41牺牲阳极电化学性能的影响[J].中国腐蚀与防护学报,1998,18(01):21-26. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%