采用超音速微粒轰击技术(SFPB)对40Cr调质钢进行表面纳米晶结构层的制备,利用TEM、XRD、GX-71型金相显微镜和TUKON2100显微/维氏硬度计等对表面纳米层的组织结构、硬度以及耐磨性进行了分析研究.结果表明:经过SFPB表面处理后,40Cr调质钢表面晶粒细化,形成了随机取向的铁素体和渗碳体纳米晶粒构成,晶粒尺寸达到10nm,纳米层厚度为40μm.纳米晶粒尺寸随着距表面距离的增加而增大,纳米化主要是位错运动的结果.经SFPB处理后,表层的显微硬度提高到526HV,且随着深度的增加,硬度迅速降低,表面的耐磨性也明显提高.
参考文献
| [1] | Lu Ke;Lv Jian .Surface nanocrystallization(SNC) of metallic materials presentation of the concept behind a new approach[J].Journal of Materials Science and Technology,1999,15(03):193-197. |
| [2] | K. Lu;J. Lu .Nanostructured surface layer on metallic materials induced by surface mechanical attrition treatment[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(0):38-45. |
| [3] | Masahide Sato;Nobuhiro Tsuji;Yoritoshi Minamino;Yuichiro Koizumi .Formation of nanocrystalline surface layers in various metallic materials by near surface severe plastic deformation[J].Science and technology of advanced materials,2004(1/2):145-152. |
| [4] | 雍兴平,刘刚,吕坚,卢柯.低碳钢表面纳米化处理及结构特征[J].金属学报,2002(02):157-160. |
| [5] | 巴德玛,马世宁,李长青,孟凡军,熊天英.超音速微粒轰击45钢表面纳米化的研究[J].材料科学与工艺,2007(03):342-346. |
| [6] | 熊天英,刘志文,李智超,吴杰,金花子,李铁藩.超音速微粒轰击金属表面纳米化新技术[J].材料导报,2003(03):69-71. |
| [7] | 黄惠忠.纳米材料分析[M].北京:化学工业出版社,2003:244. |
| [8] | 王立平,高燕,薛群基,刘惠文,徐洮.晶粒尺寸对纳米晶钴摩擦磨损性能的影响[J].表面技术,2005(01):31-33. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%