轧辊体积大且辊面状态又不好,尤其是热轧辊的表面常有氧化膜和微裂纹,在测量时又不能损伤轧辊表面,因此,轧辊残余应力的测量较困难.为验证临界折射纵波法测轧辊表面残余应力的准确性,用超声波法、X射线法和盲孔法对同一试件进行了应力测量.对这3种测量方法所测得的结果进行比较后,评价超声波法的可靠性和有效性.试验结果显示:临界折射纵波法测试的应力值与X射线衍射法和盲孔法测试的结果具有较好的一致性.
参考文献
| [1] | 虞付进,赵燕伟,张克华.超声检测表面残余应力的研究与发展[J].表面技术,2007(04):72-75. |
| [2] | Bray D E;Junghans P .Application of the LCR ultrasonic technique for evaluation of post-wela heat treatment in steel plates[J].NDT & E International,1995,28(04):235-242. |
| [3] | Donald E. Bray;N. Pathak;M.N. Srinivasan .Residual Stress Mapping in a Steam Turbine Disk Using the L_(CR) Ultrasonic Technique[J].Materials evaluation,1996(7):832-839. |
| [4] | Bray D E;Tang W;Grewal DS .Ultrasonic stress evaluation in a compressor rotor[J].Journal of Testing and Evaluation,1997,25(05):503-509. |
| [5] | Szelazek J .Ultrasonic measurement of thermal stresses in continuously welded rail[J].NDT & E International,1992,25(02):77-85. |
| [6] | Bartosiewicz A;阎锋 .超声波应力检测在铁路工业中的应用[J].国外铁道车辆,1999,36(06):33-38. |
| [7] | Don E. Bray;Wei Tang .Subsurface stress evaluation in steel plates and bars using the L_CR ultrasonic wave[J].Nuclear engineering and design,2001(2):231-240. |
| [8] | 虞付进,赵燕伟,虞先晓.超声应力检测中应力常数的标定试验研究[J].机械设计与研究,2007(04):98-101. |
| [9] | 安正植;王文宇.X射线应力测定方法[M].长春:吉林大学出版社,1990:160-208. |
| [10] | 陈怀宁;陈亮山;董秀中 .盲孔法测量残余应力的钻削加工应变[J].焊接学报,1994,15(04):276-279. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%