为了得到具有生物活性的陶瓷膜,通过研究微弧氧化的工艺条件,得到了适宜于制备钛合金生物活性膜的电解液配方,其中含20g/L Ca(CH3COO)2·H2O(乙酸钙)、9.3g/L Na5P3O10(多聚磷酸钠).结果表明:采用该电解液并在适当的微弧氧化工艺条件下,在钛合金表面制备的陶瓷膜具有多微孔结构,并且与基体结合良好,微孔分布均匀,孔径为几个微米;陶瓷膜表面含有一定比例的钙、磷元素,且钙磷比约为1.69,与羟基磷灰石中的钙磷比相当;陶瓷膜主要是由锐钛矿型和金红石型二氧化钛构成,其中以锐钛矿型二氧化钛为主.这种含有适当钙、磷元素且表层多孔的氧化钛陶瓷膜有利于骨细胞的吸附和结合.
参考文献
| [1] | 李德华 .医用钛表面的微观改造[J].国外医学(生物医学工程分册),1997,20(01):24-27. |
| [2] | 王桂生,戴经一,董辉.钛人工牙根种植体和临床应用[J].中国有色金属学报,1996(04):147-149. |
| [3] | Hcnch L L;Wilson J.An Introduction to Bioceramics[M].Singapore:World Scientific Publishing Co.Ptc.Ltd,1993:223-238. |
| [4] | Wang R R;Fen ton A .Titanium for prosthodonties applications:a review of the literature[J].Quintessencen Int,1996,27:401-408. |
| [5] | Mandl S;Sader R;Thorwarth G;Krause D;Zeilhofer HF;Horch HH;Rauschenbach B .Investigation on plasma immersion ion implantation treated medical implants.[J].Biomolecular engineering,2002(2/6):129-132. |
| [6] | 于思荣.生物医学钛合金的研究现状及发展趋势[J].材料科学与工程,2000(02):131. |
| [7] | Schreckenbach J P;Marx G;Scgkittig F.Characterization of anodic spark-onnvertted titanium surfaces for biomedical applications[J].Journal of Materials Science:Materials in Medicine,1999(10):453-457. |
| [8] | YangYungchin;Chang Edward .Measurements of residual stresses in plasma-sprayed hydroxyapatite coatings on titanium alloy[J].Surface and Coatings Technology,2005,190(01):122-131. |
| [9] | E. Gyorgy;S. Grigorescu;G. Socol;I.N. Mihailescu;D. Janackovic;A. Dindune;Z. Kanepe;E. Palcevskis;E.L. Zdrentu;S.M. Petrescu .Bioactive glass and hydroxyapatite thin films obtained by pulsed laser deposition[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2007(19):7981-7986. |
| [10] | Van T B;Brown S D;Wirtz G P .Mechanism of anodie spark deposition[J].American Ceramic Society Bulletin,1997,56(06):563-566. |
| [11] | 邓志威.微弧氧化材料表面陶瓷化机理的探讨[J].核物理动态,1997(03):193. |
| [12] | 薛文斌,邓志威,李永良,陈如意,张通和.Ti-6Al-4V在NaAlO2溶液中微弧氧化陶瓷膜的组织结构研究[J].材料科学与工艺,2000(03):41-45. |
| [13] | 薛文斌,邓志威,陈如意,张通和.钛合金在硅酸盐溶液中微弧氧化陶瓷膜的组织结构[J].金属热处理,2000(02):5-7. |
| [14] | Ward Brian C;Webster Thomas J .Increased functiona of osteoblasts on nanophase metals materials[J].Science and Engineering C,2007,27(03):575-578. |
| [15] | 旷亚非,侯朝辉,刘建平.阳极氧化过程中电击穿理论的研究进展[J].电镀与涂饰,2000(03):38-41,45. |
| [16] | 徐可为.微弧氧化生成含钙磷氧化钛生物薄膜的结构[J].无机材料学报,2001(05):951-956. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%