为了提高镁合金的耐腐蚀性能,结合硅烷处理和胶粘涂层技术在AZ31镁合金表面制备了环氧防腐涂层.通过扫描电镜对涂层表面形貌进行观察,采用划格法、浸泡法及盐雾试验等分析镁合金表面硅烷处理对有机涂层的附着力及耐蚀性的影响.研究结果表明:采用KH-550型硅烷进行处理后,镁合金基体与有机涂层之间形成化学键,涂层与基体结合牢固,附着力为1级,耐饱和盐水23d不起泡.硅烷处理明显提高了有机涂层对基体的附着力和耐蚀性,因此,硅烷 + 胶粘涂层的方法可用于镁合金的表面防腐.
The epoxy anticorrosive coating by combination silane pretreatment and adhesive coating methods was prepared on AZ31 magnesium alloy to improve its corrosion resistance. The morphology of coating was observed by SEM. The effects of silane pretreatment on the adhesion and corrosion resistance of the coating were analyzed by using scribe,immersion, salt spray tests and so on. The results show that after the pretreatment of AZ31 magnesium alloy with KH-550 silane coupling agent, there is chemical bond between the coating and the substrate, the adhesion of the coating can reach grade 1,and there is no change in saturated NaCl solution for 23d. Silane pretreatment can enhance remarkably the adhesion and corrosion resistance of the coating,so silane pretreatment and adhesive coatings are suit to magnesium alloys for protection.
参考文献
| [1] | 吴国松,曾小勤,姚寿山.AZ31镁合金表面气相沉积不锈钢薄膜的实验研究[J].材料工程,2006(z1):43-46. |
| [2] | Zhu Liqun;Song Guangling.Improved corrosion resistance of AZ91D magnesium alloy by an aluminum-alloyed coating[J].Surface and Coatings Technology,2006(200):2 834-2 840. |
| [3] | 张微,李涛,刘永丰.AZ31镁合金表面防腐胶粘涂层的研制[J].电镀与涂饰,2009(02):60-62. |
| [4] | 彭天兰,满瑞林,别子俊,琚海涛,唐翰卿,杨劲,王盼.镀锌钢板表面耐腐蚀硅烷膜的制备[J].涂料工业,2008(12):63-65. |
| [5] | 谢国先;邱大健;李朝阳.硅烷偶联剂在环氧涂料中的应用[J].电镀与涂饰,2007(04):19-21. |
| [6] | 张茹,李江华.硅烷前处理与电泳配套的涂装工艺[J].表面技术,2009(02):87-88. |
| [7] | 杨育珍;何胜刚.有机硅烷偶联剂及其应用[J].化学工程师,1994(43):40-42. |
| [8] | 翟海潮;李印柏;林新松.粘接与表面粘涂技术[M].北京:化学工业出版社,1993:7-9. |
| [9] | 丁文江.镁合金科学与技术[M].北京:科学出版社,2007:319-323. |
| [10] | 曾凡辉,姜其斌,陈宪宏.硅烷偶联剂WD-60在环氧防腐涂料中的应用[J].涂料工业,2007(01):27-28,32. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%