采用失重法、电阻法和方阻法测试碳钢在混凝土模拟溶液中的腐蚀深度,并利用极化曲线、交流阻抗测试探讨腐蚀电化学特征.在腐蚀深度为0.08 mm范围内,电阻法、方阻法与失重法测量的腐蚀深度最大差值分别为6.30μm和0.98μm,测量结果有较好的一致性.碳钢在浸泡开始时,表面有一层钝化膜,阻抗谱为单容抗弧;继续腐蚀,碳钢从钝化转变为活化,表面钝化膜遭到破坏,腐蚀溶解不断进行.
参考文献
| [1] | 金伟良;赵羽习.混凝土结构耐久性[M].北京:科学出版社,2002:93-108. |
| [2] | C. Andrade;C. Alonso;J. Sarria .Corrosion rate evolution in concrete structures exposed to the atmosphere[J].Cement & concrete composites,2002(1):55-64. |
| [3] | 孙成,李洪锡,张淑泉,高立群,黄磊,周晓晔.钢筋混凝土腐蚀研究综述[J].材料导报,2000(05):27-28,73. |
| [4] | S. Erdogdu;T.W. Bremner;I.L. Kondratova .Accelerated testing of plain and epoxy-coated reinforcement in simulated seawater and chloride solutions[J].Cement and Concrete Research,2001(6):861-867. |
| [5] | Du Ai-ling;Hou Wen-tao;Zhang He-ming et al.The Linear Polarization Method for Corrosion Rate Measurement of Reinforcing Bar of Concrete in Situ[J].Electrochemistry,2000,6(03):297-303. |
| [6] | Miguel Angel Sanjuan .Electrochemical method to assess the absorption of NaCl solutions in OPC and SRPC mortars[J].Building and environment,2000(7October):595-601. |
| [7] | A. Legat;M. Leban;Z. Bajt .Corrosion processes of steel in concrete characterized by means of electrochemical noise[J].Electrochimica Acta,2004(17/18):2741-2751. |
| [8] | 宿昌厚,鲁效明.双电测组合法测试半导体电阻率的研究[J].半导体学报,2003(03):298-306. |
| [9] | 刘新福,孙以材,刘东升.四探针技术测量薄层电阻的原理及应用[J].半导体技术,2004(07):48-52. |
| [10] | Benjamin MC;Hillard RJ;Borland JO .Ultra-shallow junction (USJ) sheet resistance measurements with a non-penetrating four point probe[J].Nuclear Instruments and Methods in Physics Research, Section B. Beam Interactions with Materials and Atoms,2005(1/2):351-355. |
| [11] | 冯长杰,杜楠,李晓刚.电阻法和方块电阻法连续监测A3钢在硫酸中的腐蚀深度[J].材料工程,2008(08):64-68. |
| [12] | 刘新福,孙以材,张艳辉,陈志永.用改进的Rymaszewski公式及方形四探针法测定微区的方块电阻[J].物理学报,2004(08):2461-2466. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%