为提高输送管道的力学性能及其陶瓷层致密度,针对纳米反应体系,采用离心自蔓延高温合成法制备出陶瓷内衬复合钢管.在纳米SiO2质量分数为6％,Ni质量分数为1％的条件下,研究了不同质量分数的纳米ZrO2添加剂,对复合管力学性能及陶瓷层致密度的影响.结果表明:加入9.5％ZrO2的复合管的压渍强度达到409 MPa,比未添加纳米ZrO2的试样提高了17.8％；当纳米ZrO2添加量为3.5％时,陶瓷层致密度达到极大值93.2％.
参考文献
| [1] | MOORE J J;FENG H J .Combustion Synthesis of Advanced Materials:Part Ⅰ:Reaction Parameters[J].Progress in Materials Science,1995,39:243-273. |
| [2] | Z. Du;H. Fu;H. Fu .A study of ceramic-lined compound copper pipe produced by SHS-centrifugal casting[J].Materials Letters,2005(14/15):1853-1858. |
| [3] | Yu-Fei Wang;Zhen-Guo Yang .Finite element analysis of residual thermal stress in ceramic-lined composite pipe prepared by centrifugal-SHS[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(0):130-134. |
| [4] | COBB P C .Titanium Carbide as a Sintering Agent for Titanium Boride[J].Materials & Design,1990,11(03):156-159. |
| [5] | 殷声,郭志猛,林涛,果世驹.陶瓷复合钢管的研究和工业应用[J].材料导报,2000(12):44-46. |
| [6] | 来永斌,陈多刚.陶瓷钢铁复合管在锅炉中的应用[J].铸造技术,2004(12):899-900. |
| [7] | 赵天林.陶瓷钢铁复合管及其在金属矿山中的应用[J].金属矿山,1997(06):38-39. |
| [8] | 张磊,焦万丽.交变磁场对SHS陶瓷复合钢管陶瓷层结构和性能的影响[J].中国有色金属学报,2009(06):1100-1104. |
| [9] | 王建江,赵忠民,叶明惠,杜心康,温晋华.机械振动对SHS陶瓷内衬复合管显微结构和力学性能的影响[J].复合材料学报,2000(02):55-59. |
| [10] | 闫红彦,潘希德,薛锦,董现春.低频机械振动对自蔓延陶瓷内衬复合管衬层性能影响研究[J].粉末冶金技术,2005(06):440-444. |
| [11] | 高翔,丘泰,焦宝祥,沈春英.纳米ZrO2对Al2O3陶瓷性能的影响[J].硅酸盐通报,2005(01):12-16. |
| [12] | 王志;赵军;邢国红 等.MF/纳米ZrO2增韧氧化铝陶瓷复合材料的力学性能[J].人工晶体学报,2009,38(08):238-241. |
| [13] | 俞建荣,张卫明,吴波,凌星中,肖云峰,王保山,郭云卿,付冉.纳米SiC对重力分离SHS陶瓷内衬复合管组织及性能的影响[J].材料保护,2009(04):64-66. |
| [14] | 朱昱,孙书刚,倪红军,黄明宇.SHS陶瓷内衬复合钢管组织和性能的研究[J].热加工工艺,2010(16):84-86. |
| [15] | 李冬黎,何湘宁.SiO2对陶瓷复合钢管孔隙度和力学性能的影响[J].机械工程材料,2001(03):32-34. |
| [16] | 郭伏安,符寒光.离心自蔓延高温合成陶瓷内衬复合钢管的研究与应用[J].湖南有色金属,2002(06):27-29,41. |
| [17] | 王志;赵军;邢国红 等.MF/纳米ZrO2增韧氧化铝陶瓷复合材料的力学性能[J].人工晶体学报,2009,38:238-241. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%