采用超音速火焰喷涂技术制备WC CrNi涂层,研究了自配副磨损和三体磨损条件下,涂层的滑动磨损性能,并分析了涂层磨损前后的形貌及成分变化.结果表明:WC-CrNi涂层组织致密、结构均匀；两种磨损条件下,涂层的摩擦系数相差较大,三体磨损时,涂层损伤严重,由于配副接触面间第三体存在增加了摩擦阻力,使得摩擦系数稳定性变差；涂层在两种磨损备件下的磨损机制有所不同,自配副时的磨损机制为WC层状剥离,三体磨损下则以微切削并伴随塑性变形为主.
参考文献
| [1] | 贺定勇,傅斌友,蒋建敏,李晓延,王智慧,栗卓新.含WC陶瓷相电弧喷涂层耐磨粒磨损性能的研究[J].摩擦学学报,2007(02):116-120. |
| [2] | 简中华,马壮,曹素红,王富耻,王全胜.超音速火焰喷涂WC-Co与NiCr-Cr2C3涂层磨损性能研究[J].材料工程,2007(07):21-24. |
| [3] | P.K. Aw;B.H. Tan .Study of microstructure, phase and microhardness distribution of HVOF sprayed multi-modal structured and conventional WC-17Co coatings[J].Journal of Materials Processing Technology,2006(1/3):305-311. |
| [4] | H. S. Sidhu;B. S. Sidhu;S. Prakash .Mechanical and microstructural properties of HVOF sprayed WC-Co and Cr_3C_2-NiCr coatings on the boiler tube steels using LPG as the fuel gas[J].Journal of Materials Processing Technology,2006(1):77-82. |
| [5] | C. N. Machio;G. Akdogan;M. J. Witcomb;S. Luyckx .Performance of WC-VC-Co thermal spray coatings in abrasion and slurry erosion tests[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2005(1/4):434-442. |
| [6] | 陈志刚,朱小蓉,汤小丽,孔德军,王玲.火焰喷涂重熔Ni基WC复合涂层的耐磨性能试验研究[J].物理学报,2007(12):7320-7329. |
| [7] | 屈金山,张晖,周仲荣.滑移区内不同堆焊层熔敷金属的微动摩擦磨损性能研究[J].摩擦学学报,2007(06):519-523. |
| [8] | 吕一中,刘俊英,曲敬信.层流等离子体射流铝合金表面熔覆SiCp/Al-Si涂层的磨损过程[J].金属热处理,2005(03):31-33. |
| [9] | CHEN Zhen-da;LIM Leong Chewh;QIAN Mingh .Laser Cladding of WC-Ni Composite[J].Journal of Materials Processing Technology,1996,62:321-323. |
| [10] | 吴萍,周昌炽,唐西南.激光熔覆镍基合金和Ni/WC涂层的磨损特性[J].金属学报,2002(12):1257-1260. |
| [11] | 蔡幼庆.等离子弧喷焊铜基合金的组织和耐磨性[J].焊接学报,2003(02):93-96. |
| [12] | 李南翔 .超音速火焰喷涂WC-Co涂层性能研究[D].大连海事大学,2010. |
| [13] | 温诗铸;黄平.摩擦学原理[M].北京:清华大学出版社,2002 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%