采用常规阳极氧化、槽压-时间曲线和电镜分析等方法，研究了铝在硫酸溶液中复合阳极氧化时Al2O3、SiC粉体细度对阳极氧化的影响。实验表明：难溶粉体细度不影响阳极氧化过程，而影响阳极氧化时的槽电压和膜层性能。粉体细，则槽电压高，膜层性能优良(硬度高、厚度大、耐蚀性好)；反之亦然。难溶粉体进入了膜层，进入量与粉体细度、粉体加入量有关。粉体粒径小、加入量大，则粉体进入膜层量也就多。
With routine anodizing, cell voltage-time curve measurement and electron microscope analysis, the effects of Al2O3, SiC insoluble powders on anodizing are researched, when Al is compositly anodized in H2SO4 solution. The tests results show that the anodizing process isn't influenced by the grain size of insoluble powders, but cell voltage of anodizing and film properties are influenced. The smaller the powder grain size, the higher the cell voltage, and the better of film properties(the hardness, thickness and anticorrosion property are all good), on the contrary, this is also right. When the insoluble powders go into film, the quantitis of entering is related to the grain size and adding quantity of insoluble powders. If the grain diameter of powders is smaller and more amount of powders are added, more powders enter the film.
参考文献
| [1] | 曾祥勇.难溶粉体对硫酸溶液中铝阳极氧化膜性能的影响[J].材料保护,1998(12):6. |
| [2] | 唐修钢;许岩;旷亚非.铝在加有难溶粉体的硫酸溶液中阳极氧化研究(Ⅰ)[A].湖南娄底,2000:103-107. |
| [3] | 李世普.特种陶瓷工艺学[M].北京:机械工业出版社,1995:89. |
| [4] | 许岩,旷亚非,刘淑坤.铝在磷酸体系中复合阳极氧化研究[J].电镀与环保,2000(02):35-37. |
| [5] | 曾祥勇 .铝在加有难溶粉体的硫酸溶液中阳极氧化研究[D].湖南大学,1998. |
| [6] | Wernick S;Pinner R;毛(动)/(灬)铭.铝及其合金的化学与电解处理[M].北京:国防工业出版社,1965:159. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%