概述了电镀铬的发展历史,简要评述了各种镀铬工艺的现状,指出了研制新型的高效、低成本镀铬添加剂的必要性.综述了镀铬添加剂的发展概况,对比分析了各类添加剂的作用,并对今后镀铬添加剂的研究做出了展望.
参考文献
| [1] | Frederick A;Lowenheim;Third Edition.Modern Electroplating[M].New York: Awiley Interscience Publication,1974:99. |
| [2] | 关山,张琦,胡如南.电镀铬的最新发展[J].材料保护,2000(03):1-3. |
| [3] | 涂洪辉,罗振华.HIL-S镀硬铬添加剂及其应用工艺[J].材料保护,1993(03):25. |
| [4] | 张允诚;胡如南;向荣.电镀[M].北京:国防工业出版社,1997:363-409. |
| [5] | 黄逢春.镀铬添加剂及镀铬工艺[J].材料保护,1996(09):14. |
| [6] | Norifumi Hatano;Akihiko Hasebe;Kazuyuki Oyama et al.Process for forming colorless chromate coating film on bright aluminum whee l[P].US:5259937,1993. |
| [7] | 杨胜奇 .浅谈稀土元素在金属表面处理领域中应用[J].电镀与环保,1995,15(04):17-18. |
| [8] | 陈永芳;江琳才.稀土阳离子作镀铬添加剂的研究[J].电镀与涂饰,1989(01):1-6. |
| [9] | 钱达人.稀土添加剂在电沉积铬层中的应用[J].材料保护,1991(03):24. |
| [10] | 张根兴.应用稀土添加剂CF-201进行低铬酸镀铬[J].材料保护,1990(03):19. |
| [11] | 陈惠国.CS型镀铬添加剂的研究[J].材料保护,1991(05):30. |
| [12] | 陈惠国.CS型镀铬添加剂的研究[J].材料保护,1991(05):30. |
| [13] | Simion Chizhevski .Electrolyte for electroplating of chromium bas ed coatinghaving improved wear resistancecorrosion resistance and plasticity[P].US:5582707,1996. |
| [14] | Hyman Chessin .Bright chromium plating baths and process[P].US:4472249,1984. |
| [15] | Anthony D;Baranyi .Hard chromium plating from hexavalent plating bath[P].US:4406756,1983. |
| [16] | Hyman Chessin;Kenneth R;Newby .Chromium plating bath for produc ing non-iridescentadherentbright chromium deposits at high efficiencies an d substantially free of cathodic low current density etching[P].US:4588481,1986. |
| [17] | Nicholas M;Martyak .High-performance electrodeposited chromium layers formed at high current efficiencies[P].US:4927506,1990. |
| [18] | Hyman Chessin .Novel low concentration decorative chromium platin g baths and method[P].US:4206019,1980. |
| [19] | Herbert A Laitinen;Shigeo Hoshino .Electrolytic bath compositio ns and method for electrodeposition of amorphous chromium[P].US 4690735,1987. |
| [20] | Ken Newby .硬铬电镀技术的发展[J].电镀与环保,1994,14(03):7-10. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%