采用电沉积方法在模拟体液中制备磷酸钙盐涂层,研究了电流密度、电解液浓度、电沉积时间以及后处理对涂层表面形貌、组分和结构的影响.研究表明:在1~10 mA/cm2电流密度下沉积60~75 min可以在模拟体液中制备结晶度较低的磷酸钙盐类涂层,涂层分别经模拟体液、碱液和水热处理后前驱体都转变为羟基磷灰石.
参考文献
[1] | Suchanek W.;Yoshimura M. .Processing and properties of hydroxyapatite-based biomaterials for use as hard tissue replacement implants [Review][J].Journal of Materials Research,1998(1):94-117. |
[2] | Ha W S;Mayer J;Koch B.Plasma-sprayed hydroxy-apatite coating on carbon fibre reinforced thermoplasatic composite materials[J].Journal of Materials Science:Materials in Medicine,1994(05):481-486. |
[3] | Ong J L;Lucas L C .Post-deposition heat treatments for ion beam sputter deposited calcium phosphate coatings[J].Biomaterials,1994,14:337-341. |
[4] | A. MONTENERO;G. GNAPPI;F. FERRARI .Sol-gel derived hydroxyapatite coatings on titanium substrate[J].Journal of Materials Science,2000(11):2791-2797. |
[5] | Ducheyne P;Radin S;Heughebaert S.Effect of calcium phosphate ceramic coatins on porous titanium[J].Biomaterials,1990(11):1415-1417. |
[6] | Shirkhanzadeh M .Bioactive calcium phosphate coa-tings prepared by electrodepositon[J].Journal of Materials Science Letters,1991,10:1415-1417. |
[7] | Shirkhanzadeh M .Calcium phosphate coatings prepared by electrocrystallization from aqueous electrolytes[J].Journal of Materials Science:Materials in Medicine,1995,6:90-93. |
[8] | 张建民.电化学法制备生物活性陶瓷材料研究[J].高等学校化学学报,1997(06):961. |
[9] | Joris S J;Amberg C H .The nature of deficiency on nonstoichiometric hydroxyapatite. Ⅱ. Spectroscopic studies of calcium and strontium hydroxyapatite[J].Journal of Physical Chemistry,1971,75:3172-3178. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%