在含有硫酸镍、钨酸钠和柠檬酸三铵的电解液中获得镍-钨合金电沉积层.在分别含有二甲基胺硼烷和二氧化锆粒子的上述电解液中,电沉积获得Ni-W-B合金和Ni-W-(ZrO2)复合镀层.采用电化学实验方法研究所获得的Ni-W、Ni-W-B和Ni-W-(ZrO2)镀层在盐酸介质中的腐蚀行为,结果表明:所获得的镀层均有较好的耐蚀性;Ni-W和Ni-W-B镀层比Ni-W-(ZrO2)镀层有较好的抗腐蚀能力.
参考文献
| [1] | Hajime Iwasaki;Kenji Higashi;T. G. Nieh .Tensile deformation and microstructure of a nanocrystalline Ni-W alloy produced by electrodeposition[J].Scripta materialia,2004(3):395-399. |
| [2] | Mikolaj Donten;Henrikas Cesiulis;Zbigniew Stojek .Electrodeposition and properties of Ni-W, Fe-W and Fe-Ni-W amorphous alloys. A comparative study[J].Electrochimica Acta,2000(20):3389-3396. |
| [3] | 杨防祖,郭逸飞,黄令,许书楷,周绍民.Electrodeposition, Structure and Corrosion Resistance of Nanocrystalline Ni-W Alloy[J].中国化学(英文版),2004(03):228-231. |
| [4] | 曹刚敏,杨防祖,黄令,牛振江,许书楷,周绍民.退火前后镍钨硼合金电沉积层的结构与性能[J].物理化学学报,2001(02):150-154. |
| [5] | Cao Gang min;Yang Fang zu;Huang Ling et al.Electrodeposition and structure of Ni-W-B amorphous alloy[J].Transactions of the Institute of Metal Finishing,2001,79(02):81-84. |
| [6] | 武刚,李宁,王殿龙,周德瑞.α-Al2O3与Co-Ni合金电化学共沉积动力学模型[J].物理化学学报,2003(11):996-1000. |
| [7] | 姚素薇;郭鹤桐;周婉秋 等.电沉积Ni-W非晶态合金[J].化工学报,1995,46(01):88-94. |
| [8] | 姚素薇;张卫国;蒋晓飞 等.非晶态合金镀层的耐蚀性能[J].天津大学学报,1999,32(03):374-377. |
| [9] | 王宙,尹桂芹,成燕.Ni-W合金镀层在1 mol/L H2SO4中的腐蚀行为[J].大连大学学报,1999(04):50-52. |
| [10] | 朱立群;李卫平;王立.硼元素对镍-钨非晶态镀层的影响[J].航空制造工程,1997(03):8-10. |
| [11] | 激光熔敷镍基合金的耐蚀性[J].中国有色金属学报,1999(02):278. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%