在不同的微蚀温度、时间条件下,研究了高锰酸钾微蚀溶液对环氧树脂层压板和3240型环氧树脂板(基板)微蚀作用的影响.通过基板表面形貌的观察和对化学镀铜层与基板间粘结强度的测定,研究和比较了高锰酸钾体系和传统的铬酐-浓硫酸体系对两种基板的微蚀效果.结果表明,经过高锰酸钾溶液处理后,环氧树脂层压板和3240型环氧板粘结强度分别可达到5.88 N/cm和2.35N/cm,远远高于传统的铬酐-浓硫酸处理后镀铜层与基板的粘结强度;同时,使用高锰酸钾溶液可以减小环境污染,且操作简单易行,它作为新型的微蚀体系有望取代传统的铬酐-浓硫酸微蚀体系.
参考文献
| [1] | Tomaiuolo F;Montangero P .Alkaline permanganate treatment in etch-back proceses[J].Transactions of The Institute of Metal Finishing,1986,64:80-84. |
| [2] | Schr(o)er D;Nichols R J;Meyer H .Pretreatment of polymer surfaces-the crucial step prior to metal deposition[J].Electrochimica Acta,1995,40:1487-1494. |
| [3] | Roizard X;Wery M;Kirmann J .Effects of the alkaline permanganate etching on the surface roughness of a fibre-reinforced epoxy composite[J].Computers and Structures,2002,56:223-228. |
| [4] | Siau S;Vervaet A;Van Vaeck L;Schacht E;Demeter U;Van Calster A .Adhesion strength of the epoxy polymer/copper interface for use in microelectronics[J].Journal of the Electrochemical Society,2005(6):C442-C455. |
| [5] | Kirmann J;Roizard X;Pagetti J et al.Effects of the alkaline pemananganate etching of epoxy on the peel adhesion of electrolessly plated copper on a fibre-reinforced epoxy composite[J].Journal of Adhesion Science and Technology,1998,12(04):383-397. |
| [6] | Mandich N V;Krulik G A .Substitution of nonhazardous for hazardous process chemicals in the printed circuit industry[J].Metal Finishing,1992,90:49-51. |
| [7] | 陈亚.现代实用电镀技术[M].北京:国防工业出版社,2003:315-316. |
| [8] | Zenglin Wang;Akihiko Furuya;Keiichirou Yasuda;Hideo Ikeda;Tomoyuki Baba;Muneaki Hagiwara;Sotaro Toki;Shoso Shingubara;Hiroshi Kubota;Tadahiro Ohmi .Adhesion improvement of electroless copper to a polyimide film substrate by combining surface microroughening and imide ring cleavage[J].Journal of Adhesion Science and Technology: The International Journal of Theoredtical and Basic Aspects of Adhesion Science and Its Applications in All Areas of Technology,2002(8):1027-1040. |
| [9] | 姜郁英.电镀塑料亚微观粗化表面参数的分析及应用[J].电镀与精饰,1995(05):12. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%