采用电沉积的方法制备了Ni-Fe合金镀层,对其微观形貌和结构进行了表征,并采用电化学方法研究了所制备的Ni-Fe合金镀层在不同介质中的腐蚀行为.结果表明:在5%硫酸溶液以及3.5%氯化钠溶液中,w(Fe)为19.23%的Ni-Fe合金镀层耐蚀性最好,在5%氢氧化钠溶液中w(Fe)为28.16%的Ni-Fe合金镀层的耐蚀性最佳.
参考文献
| [1] | 杨余芳,龚竹青,邓丽元,马玉天,阳征会.Ni-Fe合金电镀的研究进展[J].电镀与涂饰,2005(05):23-27. |
| [2] | Tomlinson W J;Campbell S A .Passivity,pitting and corrosion of anodically polarized Fe-Ni alloys in 0.5 M H2SO4 containing CI-[J].Journal of Materials Science,1986,21(07):2590-2596. |
| [3] | Flaud C;Kadri A .Influence de l'oxygene et des ions chlorure sur lecomportement electrochimique d'un alliage Fe-Ni (36% Ni) en milieu acide et neutre[J].Materials Chemistry and Physics,1983,9(06):529-537. |
| [4] | Frankei G S;Brusic V;Schad R G et al.Pitting corrosion of electroplated permalloy films[J].Corrosion Science,1993,35(1/4):63-71. |
| [5] | Ramazan Solmaz;Gulfeza Kardas .Electrochemical deposition and characterization of NiFe coatings as electrocatalytic materials for alkaline water electrolysis[J].Electrochimica Acta,2009(14):3726-3734. |
| [6] | 陈闪闪,戴品强,洪永志,郑贞.电沉积纳米晶Ni-Fe合金在碱性溶液中的腐蚀性能[J].中国表面工程,2008(05):54-58. |
| [7] | 于金库,廖波,冯皓.电沉积Ni-Fe合金及其耐蚀性的研究[J].材料保护,2002(02):30-31. |
| [8] | 张郁彬,苏长伟,张长科,周俊,何凤姣.镍铁合金的微观结构及其在3.5%氯化钠溶液中的腐蚀行为[J].电镀与涂饰,2009(12):1-4,17. |
| [9] | 王黎东,冒心远,车春波,费维栋.退火处理对Ni-Fe合金镀层织构及应力的影响[J].工程与试验,2009(03):33-36. |
| [10] | 陈天玉.镀镍合金[M].北京:化学工业出版社,2007:16-17. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%