热浸镀锌钢板在钼酸盐溶液中形成了钼酸盐化学转化膜.研究了处理液的使用寿命及成分变化对转化膜耐腐蚀性能的影响.采用极化曲线测试方法对转化膜的耐蚀性能进行评价.用电感耦合等离子体发射光谱对处理液中各成分进行分析.结果表明,新配制的500 mL钼酸盐处理液,在持续处理试样面积达到1.440 m2后失去钝化能力.扫描电镜观察发现,耐蚀性良好的转化膜表面均匀致密.电子能谱分析表明,转化膜主要由O、Zn、P和Mo元素组成.
参考文献
[1] | 李慧远.汽车用热镀锌钢板的生产及应用[J].汽车工艺与材料,2011(06):42-45. |
[2] | 邸洪双,蒋光炜,鲍成人,潘恩宝.高强钢板热镀锌工艺研究现状[J].河南冶金,2009(01):1-5. |
[3] | 赵丽新,李俊杰,申学义.镀锌钢板的应用效果[J].国外油田工程,2005(08):38-39. |
[4] | 刘艳荣,周婉秋,赵强,武士威,辛士刚.镀锌板表面无铬钝化的研究进展[J].电镀与精饰,2010(04):22-26. |
[5] | 安成强,郝建军,牟世辉.镀锌钢板无铬钝化技术的发展[J].表面技术,2003(02):6-8. |
[6] | 陈锦虹,卢锦堂,许乔瑜,孔纲,刘丽霞.镀锌层钼酸盐钝化的研究进展[J].电镀与环保,2000(01):21-24. |
[7] | Cheng-Yang Tsai;Jen-Shou Liu;Pei-Li Chen;Chao-Sung Lin .A two-step roll coating phosphate/molybdate passivation treatment for hot-dip galvanized steel sheet[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2010(10):3385-3393. |
[8] | Jin-tang L U;Zheng Z;Gang K .Microstructure and Corrosion Resistance of Lanthanum Salt Conversion Coating on Hot-Dip Galvanized Steel[J].Materials Protection,2009,4:4. |
[9] | 郭崇武,赖奂汶.镀锌层无铬钝化技术研究进展[J].全面腐蚀控制,2011(07):13-15,24. |
[10] | Liu, D.-L.;Yang, Z.-G.;Wang, Z.-Q.;Zhang, C. .Synthesis and evaluation of corrosion resistance of molybdate-based conversion coatings on electroplated zinc[J].Surface & Coatings Technology,2010(7):2328-2334. |
[11] | L. Fachikov;D. Ivanova .Surface treatment of zinc coatings by molybdate solutions[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2012(24):10160-10167. |
[12] | 宫丽,卢燕平.热镀锌钢板钼酸盐钝化膜的改性及耐蚀性[J].钢铁研究学报,2007(03):88-92. |
[13] | Wharton J A;Wilcox G D;Baldwin K R .Non-chromate conversion coating treatments for electrodeposited zincnickel alloys[J].Transactions of the Institute of Metal Finishing,1996,74:210-213. |
[14] | 卢锦堂,孔纲,陈锦虹,许乔瑜,宋进兵.热镀Zn层钼酸盐钝化工艺[J].腐蚀科学与防护技术,2001(01):46-48,41. |
[15] | 王海燕.ICP-AES的工作原理与维护保养[J].电子产品可靠性与环境试验,2010(04):60-63. |
[16] | 喻凌寒,宋之,苏流坤,吴庆晖,方军.三价铬彩锌钝化液的成分分析[J].光谱实验室,2007(05):791-794. |
[17] | 辛士刚,王莹.水中多种微量元素的直接测定[J].沈阳师范大学学报(自然科学版),2003(02):136-138. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%