为了实现在钛合金表面制备微弧氧化膜层含有特定钙、磷比例关系,指导合理配置化学试剂.研究了不同质量浓度且不同钙、磷摩尔比溶液对微弧氧化膜层中钙、磷的影响.实验结果表明,随氧化液质量浓度的升高,膜层中钙、磷含量都降低,而膜层中钙、磷比例升高.溶液中钙、磷摩尔比越高,膜层中钙、磷含量越低.若希望制备某一钙、磷摩尔比的生物膜层,可据此确定不同钙、磷摩尔比的溶液,进而确定钙、磷化合物配比关系.
参考文献
[1] | Mcpherson R;Gane N;Baatow T .Structural characteriza tion of plasma sprayed hydroxyapatite coatings[J].Jour nal of Materials Science-Materials in Medicine,1995,6(06):327-334. |
[2] | 乔洁琼,王凤彪.医用钛合金微弧氧化复合陶瓷膜层断裂力学研究[J].电镀与精饰,2012(12):18-23. |
[3] | Mendes SC;Reis RL;Bovell YP;Cunha AM;van-Blitterswijk CA;de-Bruijn JD .Biocompatibility testing of novel starch-based materials with potential application in orthopaedic surgery: a preliminary study.[J].Biomaterials,2001(14):2057-2064. |
[4] | 李慕勤,孟祥才,庄明辉,曲立杰.热处理对钛-生物玻璃涂层结合强度的影响[J].材料热处理学报,2009(02):158-161. |
[5] | Ishizawa H;Ogino M .Formation and characterization of anodic titanium oxide films containing Ca and P.[J].Journal of biomedical materials research, Part B. Applied biomaterials,1995(1):65-72. |
[6] | A. L. Yerokhin;X. Nie;A. Leyland;A. Matthews;S. J. Dowey .Plasma electrolysis for surface engineering[J].Surface & Coatings Technology,1999(2/3):73-93. |
[7] | Sul YT .The significance of the surface properties of oxidized titanium to the bone response: special emphasis on potential biochemical bonding of oxidized titanium implant.[J].Biomaterials,2003(22):3893-3907. |
[8] | 朱瑞富,王志刚,王爱娟,肖桂勇,吕宇鹏,李士同,塙隆夫.纯钛表面微弧氧化多孔陶瓷膜的结构特性[J].材料热处理学报,2009(02):129-133. |
[9] | 李夕金,程国安,薛文斌,郑瑞廷,吴晓玲,程云君.TiAl合金微弧氧化膜的制备及抗氧化性能研究[J].材料热处理学报,2006(05):95-99. |
[10] | Son W W;Zhu X;Shin H I et al.In vivo histological re sponse to anodized and anodized/hydrothermally treated titanium implants[J].JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART B-APPLIED BIOMATERIALS,2003,66B(02):520-525. |
[11] | Li LH;Kong YM;Kim HW;Kim YW;Kim HE;Heo SJ;Koak JY .Improved biological performance of Ti implants due to surface modification by micro-arc oxidation.[J].Biomaterials,2004(14):2867-2875. |
[12] | Wang F B;Di S C;Yu Jie .Biocompatibility research of medicine titanium alloy coating by microarc oxidation[J].Advanced Materials Research,2011,189(04):222-226. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%