在3.5％NaCl溶液中,用电化学方法测定了未钝化热镀锌层、钝化后烘干θ为270℃、320℃镀锌层的极化曲线;对三种镀层进行96h中性盐雾试验;用扫描电子显微镜对2种钝化膜表面形貌及成分进行分析.结果表明,在3.5％ NaCl溶液中,钝化镀层耐腐蚀性能明显优于未钝化镀层;烘干温度过高,导致钝化膜开裂严重,镀层耐腐蚀性能降低.
参考文献
| [1] | Kim H J.Development of a New Organic Composite Coated Steel Sheet with High Corrosion Resistance[J].Surface and Coatings Technology,1994(70):37-41. |
| [2] | G. D. Wilcox .Replacing Chromates for the Passivation of Zinc Surfaces[J].Transactions of the Institute of Metal Finishing,2003(1):B13-B15. |
| [3] | 曾振欧,邹锦光,赵国鹏,刘建平.镀锌层三价铬与六价铬钝化膜的性能[J].华南理工大学学报（自然科学版）,2007(05):104-108. |
| [4] | 李黎,顾宝珊,杨培燕,王宁涛.热浸镀锌及锌铝合金镀层在模拟海洋大气环境中腐蚀行为的电化学研究[J].电镀与涂饰,2011(03):40-42. |
| [5] | GB10125-1997.人造气氛腐蚀试验-盐雾试验[S]. |
| [6] | Zhang X;van den Bos C;Sloof WG;Hovestad A;Terryn H;de Wit JHW .Comparison of the morphology and corrosion performance of Cr(VI)- and Cr(III)-based conversion coatings on zinc[J].Surface & Coatings Technology,2005(1):92-104. |
| [7] | 瞿祖贵,刘俊文,许小蔓.高耐蚀性热镀锌板的钝化处理工艺探讨[J].轧钢,2002(03):19-21. |
| [8] | 任艳萍,陈锦虹.镀锌层三价铬钝化膜腐蚀行为的研究[J].材料保护,2007(02):7-10,41. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%