为了提高毛化特征轧辊的耐磨性,在制造9Cr2Mo钢轧辊表面电沉积40μm凸包状毛化铬镀层.通过电化学测试和盐雾试验研究了镀铬层和9Cr2Mo钢基体的腐蚀行为.电化学测试表明,镀铬层的耐蚀性明显优于基体.扫描电镜观测表明,经盐雾试验51h的基体出现大量腐蚀产物FeO,而镀铬层腐蚀产物细小且集中在表面裂纹附近,主要成分同样为FeO.镀铬层截面金相观察表明,盐雾通过铬层裂纹进入镀层和基体界面产生腐蚀,腐蚀产物通过裂纹通道扩散出来.
参考文献
[1] | 张佳林;耿勇.冷轧辊三种毛化工艺的比较[J].鞍钢技术,2002(1):43-46. |
[2] | 钟如涛;王玉涛;黄治军.轧辊表面激光毛化技术及装备[J].激光杂志,2010(6):54-56. |
[3] | Etsion F.State of the art in laser surface texturing[J].Journal of Tribology,20051(1):248-253. |
[4] | Elkoca O.A study on the characteristics of electrical discharge textured skin pass mill work roll[J].Surface & Coatings Technology,200812(12):2765-2774. |
[5] | A. V. Gorbunov;V. K. Belov;D. O. Begletsov.Texturing of Rollers for the Production of Auto-Industry Sheet[J].Steel in Translation,20098(8):696-699. |
[6] | C.-A. Huang;W. Lin;M.J. Liao.The electrochemical behaviour of the bright chromium deposits plated with direct- and pulse-current in 1 M H_2SO_4[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,20062(2):460-471. |
[7] | J. Simao;D. K. Aspinwall.Hard chromium plating of EDT mill work rolls[J].Journal of Materials Processing Technology,19990(0):281-287. |
[8] | 张广安;刘德志;孙荣生;蔡恒昌.镀铬轧辊在鞍钢冷轧厂2#线的应用[J].轧钢,2011(6):74-76. |
[9] | 张心华;闫爱军;聂凯斌;郑博野;陈亚琼;廖强强;姚瑶.富镍导电涂层耐腐蚀性能研究[J].涂料工业,2015(3):1-6. |
[10] | Ge HH.;Liao QQ.;Lee YG.;Loo BH.;Zhou GD..A study of anti-corrosion behavior of octadecylamine-treated iron samples[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,20001/4(1/4):39-46. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%