通过电化学恒电流法,采用苯胺-硫酸电解液在钢片表面合成聚苯胺膜,利用电化学测试技术、扫描电子显微镜、能量散射谱仪和红外光谱仪研究掺杂稀土铈对电化学合成聚苯胺膜在金属基底上的耐蚀性影响.结果表明,稀土铈的掺杂使聚苯胺膜的微观形貌由不规则团块状转变为小薄片正六边形形貌;掺杂稀土铈改性后的聚苯胺膜耐蚀性提高,其交流阻抗弧增大明显,膜层的腐蚀电位向正方向移动,腐蚀电流减小;10％ HCI点滴腐蚀t达115s.
参考文献
| [1] | Sambhu Bhadra;Dipak Khastgir;Nikhil K. Singha.Progress in preparation, processing and applications of polyaniline[J].Progress in Polymer Science,20098(8):783-810. |
| [2] | Bhavana Gupta;Rajiv Prakash.Processible polyacid doped polyaniline composites: Application for chargestorage devices[J].Materials science & engineering, C. Biomimetic and supramolecular systems,20095(5):1746-1751. |
| [3] | 王磊磊;姚超;吴凤芹;汪信;陈天虎.聚苯胺/凹凸棒石纳米导电复合材料的制备及性能研究[J].非金属矿,2010(6):22-26. |
| [4] | Jiaxing Huang;Richard B. Kaner.A General Chemical Route to Polyaniline Nanofibers[J].Journal of the American Chemical Society,20043(3):851-855. |
| [5] | 李丽;杨继萍;陈小尘;谢建云.导电聚苯胺纤维的制备与性能表征[J].高分子材料科学与工程,2011(4):151-154,158. |
| [6] | K. Kamaraj;V. Karpakam;S. Sathiyanarayanan;S. Syed Azim;G. Venkatachari.Synthesis of tungstate doped polyaniline and its usefulness in corrosion protective coatings[J].Electrochimica Acta,201125(25):9262-9268. |
| [7] | 阮孟财;缪文泉;童晓敏;施文明;张海娇.电化学方法制备聚苯胺膜及其表征[J].上海大学学报（自然科学版）,2010(5):420-425. |
| [8] | 赵晓锋;江奇;谢德钰;张;蒋海春;孙培秋;赵勇.碳纳米管/聚苯胺空心球复合材料的制备与电化学性能[J].功能材料,2010(11):1936-1939. |
| [9] | 于跃华;张玉泉;刘丽敏;李长江.聚苯胺/纳米氧化铈复合材料的合成与表征[J].高分子材料科学与工程,2005(2):170-172. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%