通过扫描电镜、透射电镜、光学金相等手段对LY12CZ铝合金疲劳短裂纹的微观机制进行了分析研究,结果表明,材料的微观组织对短裂纹扩展行为有很大影响.
参考文献
| [1] | 洪友士 等.疲劳裂纹萌生及扩展的细观过程和理论力[J].力学进展,1993,23:468-485. |
| [2] | J.C.Newman .Fastran-Ⅱ-A Fatigue Crack Growth Structural Analysis rogram[R].NASA Technical Memorandum 104159,1992. |
| [3] | J. Pearson .Inition of fatigue crack in commercial aluminium alloys and the subsequent propagation of very short crack[J].Engineering Fracture Mechanics,1975,7(02):235-247. |
| [4] | R. W. Hertyberg;W. J. Hills .Character of fatigue fracture surface micromorphology in the ultra-low growth rate regime[R].ASTM SPT 600,1976. |
| [5] | A. F. Blom;A. Hedlund;W. Zhao;A. Fathulla, B. Weiss, R. Stckler.Presented Symposium on the Behaviour of Short Fatigue Cracks[C].,1985:871-879. |
| [6] | A. Fathulla;B. Weiss;R. Stickler.Presented at the International Spring Meeting of the Sociate Francaise de Metallurage[C].,1984:541-548. |
| [7] | W. L. Morris .[J].Metallurgical and Materials Transactions,1980,11A:1117-1124. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%