采用反应溅射法制备了TiN/AlN纳米多层膜,并通过XRD,HREM和显微硬度计对多层膜的调制结构和力学性能进行了研究.结果表明:TiN/AlN纳米多层膜有较好的调制结构.小调制周期时,AlN调制层以FCC结构在TiN调制层上外延生长.调制周期增大,AlN调制层中出现六方晶型.TiN/AlN的显微硬度随调制周期的减小单调上升,并在调制周期=2nm时达到最高值HK3293.硬度的增高极有可能是小调制周期时立方AlN的形成所致.
参考文献
| [1] | Koehler J S .Attempt to design a strong solid[J].Physical Review B,1970,2:547-551. |
| [2] | Shih K K;Dove D B .Ti/Ti-N Hf/Hf-N and W/W-N multilayer films with high mechanical hardness[J].Applied Physics Letters,1992,61:654-659. |
| [3] | Tai Bor Wu .Effect of screening singularities on the elastic constants of composition-modulated alloys[J].Journal of Applied Physics,1982,53:5265-5270. |
| [4] | 李戈扬;王纪文;王公耀 等.沉积温度对Ti-B-N复合薄膜微结构及力学性能的影响[J].微细加工技术,1998,4:52-575. |
| [5] | Jonsson B;Hogmark S .Hardness measurements of thin films[J].Thin Solid Films,1984,114:257. |
| [6] | 田民波;刘德令.薄膜科学与技术手册[M].北京:机械工业出版社,1991:735. |
| [7] | Lehoczky S L .Strength enhancement in thin layered Al-Cu laminates[J].Journal of Applied Physics,1978,49(11):5479-5485. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%