采用特殊设计的夹具和疲劳测试系统,借助软X射线技术和SEM技术研究了聚酯增强橡胶的疲劳破坏机理,给出了疲劳寿命图.研究表明,定应变控制的聚酯增强橡胶的疲劳过程呈现明显的阶段性,其疲劳破坏机理表现为三种类型:基体裂纹、聚酯/橡胶界面脱粘、帘线断裂.疲劳过程的不同阶段对应不同的基体、界面以及帘线纤维的损伤机理.另外,对材料疲劳过程中的热效应进行了定性分析.
参考文献
| [1] | Crosch K .Rolling resistance and fatigue life of tires[J].Rubber Chemistry and Technology,1988,61(01):42-63. |
| [2] | Breidenbach R F;Lake G J .Mechanics of Fracture in Two-ply Laminates[J].Rubber Chemistry and Technology,1979,52(01):96-111. |
| [3] | Huang Y S;Yeoh O H .Crack Initiation and Propagation in Model Cord-Rubber Composites[J].Rubber Chemistry and Technology,1989,60:709-731. |
| [4] | Wan Z M;Du X W;Qu W;Jiang J Y,Yao M.Strain Fatigue Life and Prediction of Rayon Cord Reinforced Rubber[A].北京,1992:323-326. |
| [5] | Lee B L;Liu D S .Cumulative Damage of Fiber-reinforced Elastomer Composite Under Fatigue Loading[J].Journal of Composite Materials,1994,28(13):1261-1286. |
| [6] | 刘宇艳 .橡胶复合材料的疲劳[D].哈尔滨:哈尔滨工业大学,1998. |
| [7] | 田振辉 .聚酯帘线/橡胶复合材料疲劳特性及损伤机理研究[D].哈尔滨:哈尔滨工业大学,1997. |
| [8] | Talreja R.Fatigue of composite materials[M].Lancaster:Technomic,1987 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%