基于界面断裂力学理论,以界面的断裂能和混合度为基本细观参数,揭示了材料界面增韧的主要力学机理:一是提高界面断裂韧性,二是实现最佳断裂路径,并以此为依据, 分析了材料界面强韧化设计的主要原理和方法,为实际材料界面设计提供了理论基础.
参考文献
[1] | I W Hall;T Kyono;A Diwanji .On the fibre/matrix inte rface in boron/alum inum metal matrix composites[J].Journal of Materials Science,1987,22:1743-1748. |
[2] | C H Hsueh;P F Becher;P Angelini .[J].Journal of the American Ceramic Society,1988,71:929-933. |
[3] | C Atkinson .On quasistatic problems of cracks in a non-homogen eous elastic layer[J].Acta Mechanica,1977,26:103-113. |
[4] | F Delale;F Erdogan .On the mechanical modeling of the interf ac ial region in bonded half-planes[J].Journal of Applied Mechanics,Transactions ASME,1988,55:317-324. |
[5] | W Yang.New insights of interfacial fracture mechanics[A].London: Elsevier Pub,1991:51-56. |
[6] | W Yang;C F Shih .Fracture along an interlayer[J].International Journal of Solids and Structures,1994,31:985-1002. |
[7] | G C Papanicolaou;G J Messinis;S.S Karakatsanidis .The effect of interfa cial conditions on the elastic-longitudinal modulus of fibre reinforced composi tes[J].Journal of Materials Science,1989,24:395-401. |
[8] | P S Theocaris;T P Philippidis .Influence of the mesophases on the mechani cal properties of three-phase composites[J].Journal of Materials Science,1987,22:3407-3415. |
[9] | J W Hutchinson;Z Suo .Mixed mode cracking in layered materi als[J].Advances in Applied Mechanics,1991,28 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%