研究了SiCW/LD2复合材料管材的热挤压成形工艺.研究结果表明,采用传统的热挤压方法得到的SiCW/LD2复合材料管材外表面具有严重的表面缺陷;采用包覆挤压方法,可使 SiCW /LD2复合材料管材外表面覆盖一层均匀的铝包覆层,消除了表面缺陷,证明包覆挤压方法是一种有效的SiCW/Al复合材料管材的热挤压成形方法.
参考文献
| [1] | 武金有 .金属基复合材料及应用[J].金属成形工艺,1992,10(06):265-269. |
| [2] | M S Zedalis;J D Bryant;P S Gilman .High-Temperatur e Discotinuously Reinforced Aluminum[J].Journal of The Minerals,Metals & Materials Society,1991,8:29-31. |
| [3] | D J Lloyd .Particle Reinforced Aluminum and Magnesium Matrix Composites[J].International Materials Reviews,1994,39(01):1-23. |
| [4] | 张文龙 .SiCw/Al复合材料大应变变形和再结晶[D].哈尔滨工业大学,1999. |
| [5] | F J Humphreys;W S Miller;M R Djazeb .Microstructure a Development durin g Thermomechanical Processing of Particulate Metal-Matrix Composites[J].Materials Science and Technology,1996,6:1157-1166. |
| [6] | 张文龙,蔡柳春,彭华新,王德尊,姚忠凯.SiCW/6061Al复合材料热挤压杯及管材组织和性能[J].复合材料学报,1999(02):67-72. |
| [7] | Alan L Geiger;J Andrew Walker .The Processing and Prope r ties of Discontinuously Reinforced Aluminum composites[J].Journal of The Minerals,Metals & Materials Society,1991,8:8-15. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%