Multiphase Strengthening of Al3Ti-based Intermetallic Alloy

报导了对Al3Ti结合合金进行复相强化的研究,利用适量的Nb合金化,在L12Al3Ti基体中形成分散的第二相,其室温和高温强度显著提高,韧性也有改善.改变制备工艺,使合金发生重有序和析出过程,形成具有高度弥散微粒的复相细晶组织,合金的室温和高温强度进一步提高.并探讨了其强韧化作用机理.

[1]	Yamaguchi M;Umakoshi Y;Yamane T .[J].Philosophical Magazine A:Physics of Condensed Matter:Structure,Defects and Mechanical Properties,1987,55:301.
[2]	Morris D.G;Lerf R .[J].Philosophical Magazine A:Physics of Condensed Matter:Structure,Defects and Mechanical Properties,1991,63:1195.
[3]	Brown S.A;Kummar K.S .[J].Journal of Materials Research,1993,8:1763.
[4]	Lee K.Y;Ahn J.H .[J].Materials Science and Engineering A,1997,229:63.
[5]	Hu G.X;Sun J;Weng X.J .In High Temperature Ordered Intermetallic Alloy VI[J].Materials Research Society Symposium Proceedings,1995,364:1083.
[6]	Fu Y.Y;Hu G.X;Yang W.Y et al.[J].Acta Metall Sinica,1999,35:600.
[7]	Fu Y.Y;Shi R;Zhang J.X;Sun J. Hu G.X.[J].Intermetallics,2000(01)
[8]	Fu Y.Y;Zhang J.X;Hu G.X et al.[J].Acta Metall Sinica,2000,36:1.

上一张下一张

计量

作者相关

文章评分