Ti0.5Al0.5N涂层的抗高温氧化行为

材料工程, 2001, 1(1): 12-14. doi: 10.3969/j.issn.1001-4381.2001.01.004

Ti0.5Al0.5N涂层的抗高温氧化行为

王永康 ^1, , 雷廷权 ^2, , 夏立芳 ^3, , 熊仁章 ^4,

1.哈尔滨工业大学，哈尔滨 150001

2.哈尔滨工业大学，哈尔滨 150001

3.哈尔滨工业大学，哈尔滨 150001

4.宁波市表面工程研究中心，宁波 315041

关键词：多弧离子镀 , Ti0.5Al0.5N涂层 , 抗氧化

The Oxidation Resistant Behavior of Ti0.5Al0.5N Coating at Elevated Temperature

用AES仪研究了多弧离子镀Ti0.5Al0.5N涂层在空气气氛中的抗高温氧化行为，发现该涂层的抗高温氧化性能极其优异，其最高抗氧化温度可达800℃。采用SEM、EDX以及XTEM等方法对Ti0.5Al0.5N涂层的抗氧化机制和氧化失效机理进行了分析。

The elevated temperature oxidation resistant behavior ofTi0.5Al0.5N coating deposited by multi-arc ion deposition was studied with AES. The results show that the temperature of the highest oxidation resistant of the TiAlN coating reach 800℃. Mechanisms of oxidation resistant and failure of Ti0.5Al0.5N coating were analyzed with SEM、EDX and XTEM.

参考文献

[1]	SSant;K S Gill .Growth and Characterization of Cathodic Arc Evaporated CrN[J].Surface and Coatings Technology,1994,68-69:152-156.
[2]	YKWang;L F Xia;T Q Lei et al.AResearchonMicrostructureandPropertiesofTi,AiNCoating[J].Surface and Coatings Technology,1995,72:71-75.
[3]	B F Coll;P Sathrum et al.Optimization of Arc Evaporated (Ti,Al)N Film Composition for Cutting Tool Applications Surf & Coat Technol[J].,1992,52:57-64.
[4]	JPalmers;M V Stappen .Deposition of Ti,AlN Coatings by Means of Electron Beam Ion Plating with Evaporation of Ti and Al from Two Separate Crucibles[J].Surface and Coatings Technology,1995,76-77:363-366.
[5]	ELugscheider;O Knotek .DepositionofArcTiAlNCoatingwithPulsedBias[J].Surface and Coatings Technology,1995,76-77:700-705.

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网