因瓦合金因具有低的膨胀系数而用于制作显示器荫罩。为在200℃成形条件下建立合理的加工工艺，有必要研究它的高温响应。在加热炉内对试样进行拉伸试验，并用应变计测量。结果表明,对于790～850℃退火试样，变形抗力随加热温度从室温升至180℃而明显下降，此后在180～220℃时屈服强度与抗拉强度分别稳定在120～130MPa和300～320MPa内，且在试验条件下提高退火或加热温度，延伸率增大，但弹性模量基本不变化。
Invar alloy is employed as the material of the shadow mask of acolor picture or display tube because of its low coefficient of expansion being beneficial to the gain of high clarity . In order to provide the experimental basis for the formation of Invar alloy shadow mask at 200℃, its responses at elevated temperature were observed in the conditions of the static load and uniaxial tension by means of strain gage. The results show that for various annealing treatments at 790～850℃, the stresses is evidently dropped with increasing the heating temperature from about 20 to 180℃, and thereafter is fluctuated in 120～130MPa for the yielding strength and in 300～320MPa for the ultimate strength. The specific elongation is increased with the rise of annealing and heating temperatures, but the elastic modulus is nearly unchanged.
参考文献
| [1] | D Wenschhol.[M].Metals Handbook.9th ed,Edited by D Benjamin,ASM,1980:792. |
| [2] | 陈复民;李国俊;苏达德.弹性合金[M].上海:上海科学技术出版社,1986:642. |
| [3] | 莫洛季洛娃;简光沂.精密合金手册[M].北京:北京科学技术出版社,1989:227. |
| [4] | S Keil;O Benning .[J].Experimental Mechanics,1979,19(08):265. |
| [5] | V Dolhof.Proc of the 8th Inter Conf on Exper Stress Analysis[M].the Netherlands, Martins Nijhoff Publishers,1986:429. |
| [6] | 南俊马.测定材料屈服强度的应变计法试验研究[J].材料工程,1997(06):43. |
| [7] | 刘振兴;吴金声;刘克佩.膨胀合金手册[M].北京:冶金工业出版社,1979:23-35. |
| [8] | 黄明志;石德珂;金志浩.金属力学性能[M].西安:西安交通大学出版社,1986 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%